SABIC Innovative Plastics LNP THERMOCOMP RX00713H PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RX00713H PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* RX00713H is a compound based on Nylon 6/6 containing proprietary fillers. Characteristics of this grade are: Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D792 |
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.550 % | 0.550 % | 50% RH, 24 hrs; ASTM D570 |
| 0.810 % | 0.810 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 200 MPa | 29000 psi | Type I, 5 mm/min; ASTM D638 |
| 202 MPa | 29300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.9 % | 2.9 % | 5 mm/min; ISO 527 |
| 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 13.03 GPa | 1890 ksi | 1 mm/min; ISO 527 |
| 13.04 GPa | 1891 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 304 MPa | 44100 psi | ISO 178 |
| 309 MPa | 44800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 11.33 GPa | 1643 ksi | 2 mm/min; ISO 178 |
| 11.7 GPa | 1700 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.13 J/cm | 2.12 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 12.2 J/cm | 22.9 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² | 35.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 24.7 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 264 °C @Thickness 3.20 mm |
507 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 255 °C @Thickness 3.20 mm |
491 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 51 T 20 Polypropylene Copolymer, 20% Micronized Talc
- Taiwan PU Corporation TPUI-L70 Low Temperature Resistance, Injection Molding Polyester Base TPU
- Shakespeare FL-8 Fluorocarbon PVDF Fishing Line, 8 lb
- SSAB Tunnplat Docol® 800 DL High-strength Steel
- Techmer ES Plastiblend® PC/ABS 8800
- Teknor Apex ELEXAR® EL 8421 Thermoplastic Elastomer
- Borealis Borcoat™ BB125E Polypropylene Adhesive for Steel Pipe Coating
- Aclo Accutech Polypropylene Homopolymer HP0334T40L1 Talc Reinforced
- China-Yixing Longly Refractories 95 Alumina Ceramic Seals
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 60 PHR Carbon Black, N-990 (MT)
Copyright © lookpolymers.com All Rights Reserved