Gromax BFG30-DN00N1 Nylon 6 30% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BFG30-DN00N1 Nylon 6 30% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ISO 1183 |
| Moisture Absorption | 0.900 % | 0.900 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Temperature 80.0 °C |
0.0030 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Temperature 80.0 °C |
0.0070 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 90 | 90 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 143 MPa | 20800 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 2.6 % | 2.6 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 7.30 GPa | 1060 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 240 MPa | 34800 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 8.04 GPa | 1170 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.30 kJ/m² | 3.47 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | 6.80 J/cm² @Temperature 23.0 °C |
32.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 0.760 J/cm² @Temperature 23.0 °C |
3.62 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- PolyOne Edgetek® PC-30CF/000 BLACK Polycarbonate (PC)
- Premix Premi-Glas® 8102-20 Glass Reinforced Polyester BMC (discontinued **)
- Kinetics MIM 4605 Low Alloy Steel (As Sintered)
- Global POM-100 High Viscosity Acetal Homopolymer
- Techmer ES Elastoblend® PA6 IM 407 L
- SABIC Innovative Plastics LNP Thermocomp OFJ66 PPS - Linear
- SABIC Innovative Plastics LNP VERTON RV007E PA 66 (Europe-Africa-Middle East)
- Teknor Apex Monprene® MP 1544 Thermoplastic Elastomer
- Hexcel® HexForce™ 7562 Fiber Glass Fabric
- A. Schulman POLYPUR™ FPU 1152C Thermoplastic Polyurethane
Copyright © lookpolymers.com All Rights Reserved