Gichem GILAC F120 Acrylonitrile Butadiene Styrene (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gichem GILAC F120 Acrylonitrile Butadiene Styrene
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ABS high fluidity, good stiffness and excellent stampability. Medium-High Injection speed.Information provided by GICHEM Gruppo Industriale Chimico
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 25 g/10 min | 25 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ASTM D638 |
| Elongation at Yield | 30 % | 30 % | ASTM D638 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM D790 |
| Izod Impact, Notched | 1.20 J/cm | 2.25 ft-lb/in | ASTM D256 |
| 0.700 J/cm @Temperature 0.000 °C |
1.31 ft-lb/in @Temperature 32.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ASTM D648 |
| Vicat Softening Point | 96.0 °C | 205 °F | ASTM D1525/A |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
|
| Flammability Test | 75 | 75 | [°C] Bilia; IEC 331 |
| Oxygen Index | 19 % | 19 % | ASTM D2863 |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 220 °C | 428 °F | |
| Mold Temperature | 50.0 - 60.0 °C | 122 - 140 °F | |
| Drying Temperature | 80.0 °C | 176 °F | 2 hours |
Users viewing this material also viewed the following:
- Plastcom SLOVASTER® B2 GF 10 PBT, 10% glass fibre
- Lehmann & Voss LUVOCOM® 1105-0918/EM/BL PEEK, with glass fiber
- Styron Magnumâ„¢ 9095 ABS, High Gloss
- Techmer ES Elastoblend® PA6/6 GF33 IM HS L BK 33% Glass Filled
- A. Schulman PP 1329H-01 Polypropylene Medium Impact Polypropylene
- A. Schulman POLYBATCH™ Green 300 Concentrate Based In Polyethylene
- Chengdu Polyster 20 LPI Lenticular Lens Sheet, PS
- Eurotec® Tecomid® NA40 GR50 NL PA 6.6 50% glass fiber reinforced
- Colorite Polymers 8090C General Purpose Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved