Styron PULSEâ„¢ 6000 BG PC/ABS Engineering Resin
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | PULSE™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron PULSEâ„¢ 6000 BG PC/ABS Engineering Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Overview: PULSE 6000 BG is a PC/ABS resin offering an interesting combination of heat ageing characteristics, low temperature impact performance and high melt strength. Its low MFR enables manufacturing of complex blow molding parts.Applications: Blow Molded Spoilers, knee bolsters and Seat Backs.Information provided by Styron
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792; ISO 1183 |
| Water Absorption | 0.53 % @Temperature 23.0 °C, Time 86400 sec |
0.53 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ISO 527-2 |
| 54.5 MPa | 7900 psi | ASTM D638 | |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | ASTM D638 |
| 54.0 MPa | 7830 psi | ISO 527-2 | |
| Elongation at Break | >= 80 % | >= 80 % | ISO 527-2; ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527-2; ASTM D638 |
| Tensile Modulus | 2.16 GPa | 313 ksi | ASTM D638 |
| 2.28 GPa | 331 ksi | ISO 527-2 | |
| Flexural Strength | 68.0 MPa | 9860 psi | 3 points, 2 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 3 points, 2 mm/min; ISO 178 |
| Izod Impact, Notched | 6.40 J/cm @Temperature -40.0 °C |
12.0 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| 7.50 J/cm @Temperature 23.0 °C |
14.1 ft-lb/in @Temperature 73.4 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 61.0 kJ/m² @Temperature -40.0 °C |
29.0 ft-lb/in² @Temperature -40.0 °F |
ASTM D256 |
| 69.0 kJ/m² @Temperature 23.0 °C |
32.8 ft-lb/in² @Temperature 73.4 °F |
ASTM D256 | |
| Charpy Impact, Notched | 5.00 J/cm² @Temperature -40.0 °C |
23.8 ft-lb/in² @Temperature -40.0 °F |
ISO 179 |
| 6.10 J/cm² @Temperature 23.0 °C |
29.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 74.0 µm/m-°C @Temperature -40.0 - 82.0 °C |
41.1 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | Unannealed; ISO 75-2/B |
| 111 °C | 232 °F | Unannealed; ASTM D648 | |
| Vicat Softening Point | 130 °C | 266 °F | ISO 306/B50 |
| 144 °C | 291 °F | ISO 306/A120 |
Users viewing this material also viewed the following:
- Mearthane Durethaneâ„¢ S DS-285A Solid Polyurethane Elastomer
- Multibase Multibatch® ME 50043 Anti-blocking Masterbatch
- SGL Carbon Group PANOX® LB C076 SSC Oxidized Textile Fiber, Crimped staple fiber, For felts and non-wovens
- Solvay Chemicals SOLKANE® 365mfc Component for Solvent Formulation
- Saint-Gobain CHR® 280-6(R) Roll Covering Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Hexcel® HexWeb® HRH-310 - 1/8 - 1.8 Aramid Fiber/Polyimide Resin Honeycomb
- Covestro Makrolon® FR6901 Polycarbonate
- DSM Stanyl® 46HF4130 Nylon 46-30% Glass Reinforced (European and Asian Grade) (Dry)
- ExxonMobil 24 Mobil Mist Lube Series
Copyright © lookpolymers.com All Rights Reserved