SABIC Innovative Plastics LNP COLORCOMP JX91550 PES (Asia Pacific)

Category Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Colorcomp
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP COLORCOMP JX91550 PES (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP COLORCOMP* JX91550 is a compound based on Polyethersulfone resin containing Unfilled Custom Color.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
ASTM D792
1.49 g/cc
0.0538 lb/in³
ISO 1183
Moisture Absorption 0.760 %
0.760 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
0.0060 - 0.0080 in/in

@Time 24.0 hour
ASTM D955
0.0060 - 0.0080 cm/cm

@Time 86400 sec
0.0060 - 0.0080 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0070 - 0.0090 cm/cm

@Time 86400 sec
0.0070 - 0.0090 in/in

@Time 24.0 hour
ASTM D955
0.0070 - 0.0090 cm/cm

@Time 86400 sec
0.0070 - 0.0090 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.0 MPa
7690 psi
ISO 527
58.0 MPa
8410 psi
ASTM D638
Tensile Strength, Yield 77.0 MPa
11200 psi
ASTM D638
78.0 MPa
11300 psi
ISO 527
Elongation at Break 13.5 %
13.5 %
ASTM D638
23.4 %
23.4 %
ISO 527
Elongation at Yield 5.6 %
5.6 %
ASTM D638
6.2 %
6.2 %
ISO 527
Tensile Modulus 2.83 GPa
410 ksi
1 mm/min; ISO 527
2.93 GPa
425 ksi
50 mm/min; ASTM D638
Flexural Strength 118 MPa
17100 psi
ISO 178
122 MPa
17700 psi
ASTM D790
Flexural Modulus 2.89 GPa
419 ksi
ASTM D790
2.92 GPa
424 ksi
ISO 178
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*4; ISO 180/1U
Dart Drop, Total Energy 19.0 J
14.0 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 32.0 J
23.6 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
28.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
50.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
28.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 51.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
28.6 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
51.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
28.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 187 °C
369 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
176 °C

@Thickness 3.20 mm
349 °F

@Thickness 0.126 in
unannealed; ASTM D648