- Asahi Kasei Thermylene® P6-30FG-0687 30% Glass Fiber Reinforced, Heat Stabilized
Asahi Kasei Thermylene® P6-30FG-0687 30% Glass Fiber Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Asahi Kasei |
| Trade Name | Thermylene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Thermylene® P6-30FG-0687 30% Glass Fiber Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asahi Thermofil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength, Yield | 93.1 MPa | 13500 psi | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 5.24 GPa | 760 ksi | ASTM D638 |
| Flexural Strength | 131 MPa | 19000 psi | ASTM D790 |
| Flexural Modulus | 5.31 GPa | 770 ksi | ASTM D790 |
| Izod Impact, Notched | 1.01 J/cm | 1.90 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.94 J/cm | 13.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 37.8 µm/m-°C @Temperature 20.0 °C |
21.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
| Flame Spread | 36 mm/min | 1.4 in/min | Horizontal Burn Rate; FMVSS302 |
Users viewing this material also viewed the following:
- Raschig Group EN 5007 Epoxy Molding Compound
- Gouda Vuurvast CURAS SiC 70 D Moldable Refractory Material
- Styron XZ 94462.01 Carboxylated SB
- ExxonMobil Mobil 1 10W-40 Motorcycle Oil MX4T 4-Cycle
- Beijing Ranger Chem 199 Solid Epoxy Resin
- Bhansali Engineering Abstron HR-59 ABS Heat Resistant
- A. Schulman ComAlloy Comtuf® 109 Polypropylene, Mineral Reinforced, Impact Modified
- 3M Scotch® 827 Pouch Tape
- Eastman Tenite Butyrate 465A3720010 Clear, Trsp Cellulose Acetate Butyrate (discontinued **)
Copyright © lookpolymers.com All Rights Reserved