Firestone CLM200-001 Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Firestone |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Firestone CLM200-001 Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Used for monofiliament extrusion. Natural color. Not heat stabilized or modified. Lubricated. Chip size is 2 x 3.5 mm.Information provided by Firestone
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Viscosity Measurement | 3.2 | 3.2 | Relative Viscosity; Sulfuric Acid |
| 82 | 82 | Relative Viscosity; Formic Acid | |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 81.4 MPa | 11800 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Strength | 103 MPa | 15000 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 238 - 249 °C | 460 - 480 °F | |
| Middle Barrel Temperature | 238 - 249 °C | 460 - 480 °F | |
| Front Barrel Temperature | 243 - 260 °C | 470 - 500 °F | |
| Nozzle Temperature | 249 - 260 °C | 480 - 500 °F | |
| Melt Temperature | 249 - 260 °C | 480 - 500 °F | |
| Mold Temperature | 48.9 - 82.2 °C | 120 - 180 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | <= 0.080 % | <= 0.080 % |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® GX3800F ABS
- Nilit FRIANYL A63 M2 Nylon 6.6 for injection molding, 2% molybdenum disulphide lubricated
- SABIC Innovative Plastics LNP LUBRICOMP AI0019 ABS (Europe-Africa-Middle East)
- Fainplast Compounds RE 337 Rigid PVC, Extrusion
- SABIC Innovative Plastics LNP THERMOCOMP DZ004 PC (Asia Pacific)
- Universal Wire Works ER320LR Stainless Steel Bare Wire
- ExxonMobil Label-Lyte® 70 LS-447 Matte Finish, Coated, White Opaque, Sheetable OPP
- CEN® Electronic Material CF 200CF919 Polyimide Film
Copyright © lookpolymers.com All Rights Reserved