ExxonMobil Vyram™ 9101-55 Thermoplastic Elastomer  (discontinued **)

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Vulcanizate Elastomer (TPV)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Vyram™ 9101-55 Thermoplastic Elastomer  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
A soft, black, versatile thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. It is designed for applications requiring good flexibility, appearance and sealing characteristics. This grade of Vyram TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding or extrusion. It is polyolefin based and completely recyclable.Information provided by Advanced Elastomer Systems
Physical Properties Metric English Comments
Specific Gravity 1.00 g/cc
1.00 g/cc
23°C; ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore A 55
55
.12 in; ASTM D2240
60
60
302°F, 168 hr; ASTM D573
Tensile Strength at Break 4.21 MPa
610 psi
Across Flow; ASTM D412
4.584 MPa
664.9 psi
302°F, 168 hr; ASTM D573
Tensile Strength, Ultimate 1.79 MPa
260 psi
Across Flow; ASTM D412
Elongation at Break 460 %
460 %
Across Flow; ASTM D412
634.8 %
634.8 %
302°F, 168 hr; ASTM D573
Tear Strength 23.0 kN/m
131 pli
73°F, Die C; ASTM D624
Compression Set 18 %
18 %
73°F, 22 hr; ASTM D395
43 %
43 %
212°F, 70 hr; ASTM D395
Thermal Properties Metric English Comments
Brittleness Temperature -67.8 °C
-90.0 °F
ASTM 746
Processing Properties Metric English Comments
Processing Temperature 175 - 230 °C
347 - 446 °F
Rear Barrel Temperature 188 °C
370 °F
Middle Barrel Temperature 191 °C
375 °F
Front Barrel Temperature 193 °C
380 °F
Nozzle Temperature 199 °C
390 °F
Die Temperature 204 °C
400 °F
Extrusion
Melt Temperature 177 - 204 °C
350 - 400 °F
Extrusion
204 °C
400 °F
Mold Temperature 10.0 - 51.7 °C
50.0 - 125 °F
Processing
Drying Temperature 82.2 °C
180 °F
Dry Time 3 hour
3 hour
Moisture Content 0.080 %
0.080 %
Back Pressure 0.345 - 0.689 MPa
50.0 - 100 psi
Processing
5.00 - 20.0 MPa
725 - 2900 psi
Extrusion
Clamp Pressure 41.4 - 68.9 MPa
6000 - 10000 psi
Vent Depth 0.00254 cm
0.00100 in
Cushion 0.317 - 0.635 cm
0.125 - 0.250 in
Screw Speed 100 - 200 rpm
100 - 200 rpm
Descriptive Properties Value Comments
Color Black
Form Pellets
Injection Rate Fast
Maximum Regrind % 20
Screw Compression Ratio 2:1 - 2.5:1
Screw L/D Ratio 16:1 - 20:1