- Eurotec® Tecomid® NT40 GR60 NL HS PPA, 60% glass fiber reinforced, heat stabilized, natural
Eurotec® Tecomid® NT40 GR60 NL HS PPA, 60% glass fiber reinforced, heat stabilized, natural
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | Eurotec |
| Trade Name | Tecomid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecomid® NT40 GR60 NL HS PPA, 60% glass fiber reinforced, heat stabilized, natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.75 g/cc | 0.0632 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.00 % @Temperature 23.0 °C |
1.00 % @Temperature 73.4 °F |
50% RH; ISO 960 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | Eurotec |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | Eurotec |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 275 MPa | 39900 psi | ISO 527 |
| Elongation at Break | 1.5 % | 1.5 % | ISO 527 |
| Tensile Modulus | 22.0 GPa | 3190 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 315 °C | 599 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 305 °C | 581 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75 |
| Vicat Softening Point | 295 °C @Load 5.10 kg |
563 °F @Load 11.2 lb |
ISO 306 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Comparative Tracking Index | 550 V | 550 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 320 - 340 °C | 608 - 644 °F | |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Throat |
| Mold Temperature | 140 - 180 °C | 284 - 356 °F | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 4.00 hour | 4.00 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | ISO 960 |
| Hold Pressure | 40.0 - 80.0 MPa | 5800 - 11600 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Fast |
Users viewing this material also viewed the following:
- Samyang Triloy® 410N PC/PET alloy, Flame Retardant (discontinued **)
- Mid-Mountain Materials CERMEX® MT1800 Needled Silica Mat
- Lucas-Milhaupt Silvaloy® A45 Brazing Alloy
- Lucent Polymers LPB-130 Polybutylene Terephthalate, 30% Glass Fiber/Mineral Reinforced, Low Warp
- H.C. Starck Baymetec® Niobium Ethoxide
- DuPont Nucrel® 3990 Ethylene-Acrylic Acid Copolymer Resin for Extrusion Coating/Laminating
- Ter Hell Plastic Terez® PA 6.6 7750 T Polyamide 66
- Aclo Accutech Polypropylene Homopolymer HP0336W20L1 Wollastonite Reinforced
- BASF Ultramid® A3HG7 BK 00564 35% Glass Filled PA66 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved