- Eurotec® Tecomid® NT40 GR30 NL XA60 PPA, 30% glass fiber reinforced, flame retardant - halogen & red phosphorus free, heat stabilized, natural
Eurotec® Tecomid® NT40 GR30 NL XA60 PPA, 30% glass fiber reinforced, flame retardant - halogen & red phosphorus free, heat stabilized, natural
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced |
| Manufacturer | Eurotec |
| Trade Name | Tecomid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecomid® NT40 GR30 NL XA60 PPA, 30% glass fiber reinforced, flame retardant - halogen & red phosphorus free, heat stabilized, natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.30 % @Temperature 23.0 °C |
1.30 % @Temperature 73.4 °F |
50% RH; ISO 960 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | Eurotec |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | Eurotec |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 170 MPa | 24700 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| Tensile Modulus | 11.5 GPa | 1670 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 8.00 kJ/m² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 315 °C | 599 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ISO 75 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
|
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
||
| Glow Wire Test | 850 °C @Thickness 2.00 mm |
1560 °F @Thickness 0.0787 in |
GWIT; IEC 60695 |
| 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
GWFI; IEC 60695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 320 - 330 °C | 608 - 626 °F | |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Throat |
| Mold Temperature | 140 - 180 °C | 284 - 356 °F | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 4.00 hour | 4.00 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | ISO 960 |
| Hold Pressure | 40.0 - 80.0 MPa | 5800 - 11600 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Fast |
Users viewing this material also viewed the following:
- Noble Polymers Ecobarrier™ 2412 Thermoplastic Olefin (TPO)
- PolyOne Geon™ Vinyl Flexible R100AE Polyvinyl Chloride, Flexible (PVC, Flexible)
- Total Finathene® LL 4010 FH 18 LLDPE film (discontinued **)
- LG Chemical LUMID GP2330BL PA66+GF33%, General Purpose
- Lubriplate CP-8A Petroleum-Based Gear, Bearing, & Recirculating Oil
- Teknor Apex Terraloy™ BP 18003A Thermoplastic Starch + HIPS
- Lubrizol ESTANE® 58370 Ether Based Thermoplastic Polyurethane (European Grade)
- ExxonMobil Label-Lyte™ 38LL247 OPP Film
- EMS-Griltech Grilene® KE 150 CoPES Mono-Component Fusible Adhesive Fiber
- Fainplast Compounds KL 94 Flexible PVC, Insulation for High Temperatures Lead Free
Copyright © lookpolymers.com All Rights Reserved