- Barlog Plastics KEBAFORM C 906 GB POM Copolymer, 30% glass bead reinforced
Barlog Plastics KEBAFORM C 906 GB POM Copolymer, 30% glass bead reinforced
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Glass Bead Filled |
| Manufacturer | Barlog Plastics |
| Trade Name | KEBAFORM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Barlog Plastics KEBAFORM C 906 GB POM Copolymer, 30% glass bead reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
POM-GB30Information provided by BARLOG plastics GmbH.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.16 % | 0.16 % | similar to ISO 62 test |
| Linear Mold Shrinkage, Flow | 0.017 cm/cm | 0.017 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ISO 294-4 |
| Melt Flow | 22 g/10 min @Load 2.16 kg, Temperature 190 °C |
22 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ISO 527-1 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527-1 |
| Tensile Modulus | 3.80 GPa | 551 ksi | ISO 527-1 |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179-1eU |
| Charpy Impact, Notched | 0.250 J/cm² | 1.19 ft-lb/in² | ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 166 °C | 331 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C | 234 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Type | POM-GB30 |
Users viewing this material also viewed the following:
- MV Labs ND880 Nd(OH)3·xH2O Neodymium(III) hydroxide hydrate
- Reltek BONDiT™ B-482TH Adhesive and Sealant
- Lehmann & Voss LUVOCOM® 1105/GF/30/BK-1 PEEK, with glass fiber
- SABIC Innovative Plastics Ultem HATX100 PEI+PCE (Asia Pacific)
- Saint-Gobain Chemfab® 3 Basic PTFE-Coated Glass
- ExxonMobil Mobil Almo 527
- Covestro Makrofol® BL 6-2 820803 Polycarbonate
- Eurotec® Tecomid® NB40 NL FY50 PA6, unfilled, flame retardant - halogen & red phosphorus free, natural
Copyright © lookpolymers.com All Rights Reserved