- Eurotec® Tecoform® PO30 GB30 NL HS POM, 30% glass bead reinforced, heat stabilized, natural
Eurotec® Tecoform® PO30 GB30 NL HS POM, 30% glass bead reinforced, heat stabilized, natural
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Glass Bead Filled |
| Manufacturer | Eurotec |
| Trade Name | Tecoform® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecoform® PO30 GB30 NL HS POM, 30% glass bead reinforced, heat stabilized, natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.200 % @Temperature 23.0 °C |
0.200 % @Temperature 73.4 °F |
50% RH; ISO 960 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | Eurotec |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | Eurotec |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Break | 10 % | 10 % | ISO 527 |
| Tensile Modulus | 3.50 GPa | 508 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
| Comparative Tracking Index | 500 V | 500 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 190 - 230 °C | 374 - 446 °F | |
| Feed Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | Throat |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | |
| Drying Temperature | 100 - 120 °C | 212 - 248 °F | |
| Dry Time | 3.00 - 6.00 hour | 3.00 - 6.00 hour | |
| Hold Pressure | 80.0 - 100 MPa | 11600 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Medium - Fast |
Users viewing this material also viewed the following:
- Nye Lubricants 708D (NG) Synthetic Oil
- Total Finathene® 2344 HDPE film (discontinued **)
- Arkema Group Kynar Flex® 3120 PVDF Copolymer (discontinued **)
- Lubriplate L0750 Heat Transfer Oil Specialty Oil and Fluid
- SABIC Innovative Plastics LNP Thermocomp RF006PS PA 66
- Silikony Polskie Polsil OM 3000 Methyl Silicone Fluid
- TIMCAL TIMREX® T150 Primary Synthetic Graphite
- Unitika elitel UE3700 Polyester, Pellet
- A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66
- EMS-Grivory Grivory® L 20 GM PA12
Copyright © lookpolymers.com All Rights Reserved