Eurotec® Tecoform® PO20 NL RT POM, PTFE modified, natural
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, PTFE Filled |
| Manufacturer | Eurotec |
| Trade Name | Tecoform® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecoform® PO20 NL RT POM, PTFE modified, natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.200 % @Temperature 23.0 °C |
0.200 % @Temperature 73.4 °F |
50% RH; ISO 960 |
| Linear Mold Shrinkage, Flow | 0.019 cm/cm | 0.019 in/in | Eurotec |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in | Eurotec |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527 |
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 180 - 220 °C | 356 - 428 °F | |
| Feed Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | Throat |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 100 - 120 °C | 212 - 248 °F | |
| Dry Time | 3.00 - 6.00 hour | 3.00 - 6.00 hour | |
| Hold Pressure | 80.0 - 100 MPa | 11600 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Medium - Fast |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible 90034 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Techmer ES Elastoblend® PA6/6 GF43 IM L 43% Glass Filled
- Saint-Gobain CHR® 2302-5R UHMW Film Backing Acrylic Adhesive Pressure Sensitive Tape
- ExxonMobil SAE 40 Mobilgard ADL Series
- Westlake Hifor LT74147 Linear Low Density Polyethylene
- Total PSC 1340 Crystal Polystyrene
- A. Schulman POLYFORT™ FPP 1200 Calcium Carbonate-Filled Homopolymer Polypropylene
- Dow Corning SILASTIC® M RTV SILICONE RUBBER BASE & CURING AGENT (BLUE)
- CLAL-MSX ARCAP Anticorrosion AP1 H11 1/4 hard, Rolled Copper Alloy
- ConocoPhillips Hydroclear® 320 6 EP gear Oil
Copyright © lookpolymers.com All Rights Reserved