Eurostar Starpylen M1000-BK1A987 PP, Carbon Black
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starpylen |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starpylen M1000-BK1A987 PP, Carbon Black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starpylen M1000-BK1A987 is a high carbon black load PP resinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.015 - 0.020 cm/cm @Thickness 3.00 mm |
0.015 - 0.020 in/in @Thickness 0.118 in |
|
| Melt Flow | 6.0 - 12 g/10 min @Load 5.00 kg, Temperature 230 °C |
6.0 - 12 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 35.0 MPa | 5080 psi | ISO 527 |
| Elongation at Break | >= 9.0 % | >= 9.0 % | ISO 527 |
| Flexural Strength | 54.0 MPa | 7830 psi | ISO 178 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ISO 178 |
| Izod Impact, Unnotched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80x10x4; ISO 180/1U |
| Charpy Impact Unnotched | 0.900 J/cm² | 4.28 ft-lb/in² | Edgew 80x10x4 sp=62; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 220 - 230 °C | 428 - 446 °F | |
| Zone 2 | 220 - 230 °C | 428 - 446 °F | |
| Zone 3 | 220 - 230 °C | 428 - 446 °F | |
| Melt Temperature | 220 - 230 °C | 428 - 446 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |
| Drying Temperature | 70.0 °C @Time 10800 sec |
158 °F @Time 3.00 hour |
Users viewing this material also viewed the following:
- Nylene® 609 Nylon 6, Film/Extrusion Grade
- NanoScale NanoActive® Magnesium Oxide
- ExxonMobil Escorene® CR-5810 EVA Resin, for High Cling Stretch Film (discontinued **)
- Lehmann & Voss LUVOCOM® 3-7088/GY7012 Polyamide 6, with carbon fiber and glass fiber, low-warpage
- MarkeTech Neodymium Gallium Oxide (NdGaO3) Single Crystal Substrate
- Sumitomo Chemical ESPOLEX® 3675 Thermoplastic Elastomer
- Dow Corning SILASTIC® Q7-4850 BIOMEDICAL GRADE ETR ELASTOMER, KIT
- ELASTO UK Dryflex® 650800 TPE, Improved Compression Set and High Temperature Resistance, 80A Hardness
Copyright © lookpolymers.com All Rights Reserved