Eurostar Starflam PZ00062E PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam PZ00062E PA6, Glass Fiber Filled, Flame Retardant, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam PX0062E is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Time 86400 sec |
0.0020 - 0.0050 in/in @Time 24.0 hour |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| Tensile Modulus | 8.10 GPa | 1170 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
| Flexural Modulus | 7.30 GPa | 1060 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 240 - 250 °C | 464 - 482 °F | |
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Poco Graphite SCF-2 Ion Implant Grade Graphite
- SABIC Innovative Plastics Lexan® HPM1944 PC
- Overview of materials for Nylon 66, Mineral Filled, Impact Grade
- Gwent Electronic Materials D2030210D1 Polymer Dielectric
- Eagle Brass 102 OF COPPER (Non-Certified), Extra Spring
- 3M Controltac™ 8620Cv2 ES Changeable Graphic Film with Comply™ v2 Adhesive
- Aptek 7504LM-PMF UV Urethane Coating/Encapsulant
- Overview of materials for Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced
- Polymer Resources PPX-G20 Modified PPO, 20% Glass Reinforced (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved