- Eurostar Starflam PFB139E PA6, Glass Fiber/Bead Filled, Flame Retardant, Injection Molded
Eurostar Starflam PFB139E PA6, Glass Fiber/Bead Filled, Flame Retardant, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam PFB139E PA6, Glass Fiber/Bead Filled, Flame Retardant, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam PFB139E is a Flame Retardant Glass Bead and Glass Fiber Reinforced Polyamide 6 Injection Molding Resin (also known as PFB1013Z590)Information provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| Water Absorption | 1.3 % @Temperature 23.0 °C, Time 86400 sec |
1.3 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 4.00 mm |
0.0030 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 121 MPa | 17500 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 121 MPa | 17500 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.7 % | 2.7 % | 5 mm/min; ISO 527 |
| 3.5 % | 3.5 % | Flexural, 2 mm/min; ISO 178 | |
| Elongation at Yield | 2.7 % | 2.7 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 6.80 GPa | 986 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 169 MPa | 24500 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 170 MPa | 24700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.90 GPa | 856 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
23.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 97.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
53.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 203 °C | 397 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 240 - 250 °C | 464 - 482 °F | |
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Resin Technology Group 1109-DP Oxy-Bond™ Two-Component Epoxy Adhesive
- Plaslok 309 Black (INJ) Mineral/Fiber Filled Phenolic Molding Compound (discontinued **)
- Lehmann & Voss LUVOCOM® 1850-7315 PBT, with carbon fiber
- Haysite H1000 Polyester Laminate
- LyondellBasell Hifaxâ„¢ ETA-3081 Thermoplastic Olefin Resin
- Henkel Frekote 700-NC Mold Release Agent
- ThyssenKrupp SECURE 600 Structural Steel
- Braskem Green PE SHA7260 Injection Molding High Density Polyethylene
- Aclo Accutech Polypropylene Homopolymer HP0336T20L Talc Reinforced
- DuPont Performance Polymers Hytrel® 4068FG TPC-ET (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved