Eurostar Starflam MX06101 PP, Flame Retardant, Injection Molding
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam MX06101 PP, Flame Retardant, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam MX06101 is an Unfilled, Halogen Free Flame Retardant Polypropylene Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm @Thickness 4.00 mm |
0.018 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 17.0 MPa | 2470 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 24 % | 24 % | 50 mm/min; ISO 527 |
| Flexural Yield Strength | 26.0 MPa | 3770 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.50 GPa | 218 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 160 - 170 °C | 320 - 338 °F | |
| Zone 2 | 170 - 180 °C | 338 - 356 °F | |
| Zone 3 | 180 - 190 °C | 356 - 374 °F | |
| Melt Temperature | 170 - 190 °C | 338 - 374 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |
| Drying Temperature | 70.0 °C @Time 10800 sec |
158 °F @Time 3.00 hour |
Users viewing this material also viewed the following:
- Techmer ES Luriblend® POM HO TL10 Acetal
- Schmolz + Bickenbach UGIMA® 316/316L Stainless Steel Bar
- A. Schulman POLYBATCH™ Gardenia P80515PF Concentrate Based In Polypropylene
- Chosun Refractories C18D Magnesia Carbon Brick for Converter
- Chosun Refractories PCB-50 Casting Block
- DuPont Teijin Films Mylar® EB11 Polyester Film, 48 Gauge
- BASF Ultramid® B40 01 PA6 (Dry)
- Overview of materials for Linear Low Density Polyethylene (LLDPE), Sheeting Grade
Copyright © lookpolymers.com All Rights Reserved