Eurostar Starflam AFR200Y PA66, Flame Retardant, Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam AFR200Y PA66, Flame Retardant, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide AFR200Y is an Unfilled, Halogen Free and Red Phosphorous Free, Flame Retardant Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.10 % @Temperature 23.0 °C |
1.10 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 7.5 % @Temperature 23.0 °C |
7.5 % @Temperature 73.4 °F |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.011 - 0.015 cm/cm | 0.011 - 0.015 in/in | on Tensile Bar; E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ISO 2039-2 |
| Tensile Strength at Break | 78.0 MPa | 11300 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 9.0 % | 9.0 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 4.8 % | 4.8 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 3.40 GPa | 493 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 120 MPa | 17400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.30 GPa | 479 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1A |
| 3.00 kJ/m² @Temperature -40.0 °C |
1.43 ft-lb/in² @Temperature -40.0 °F |
80x10x4; ISO 180/1A | |
| 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A | |
| 4.00 kJ/m² @Temperature -20.0 °C |
1.90 ft-lb/in² @Temperature -4.00 °F |
80x10x4; ISO 180/1A | |
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU |
| >= 10.0 J/cm² @Temperature 23.0 °C |
>= 47.6 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU | |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA |
| 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA | |
| Taber Abrasion, mg/1000 Cycles | 24 @Load 1.00 kg |
24 @Load 2.20 lb |
CS-17; E2P Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 85.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 85.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Hot Ball Pressure Test | 123 - 127 °C | 253 - 261 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Vicat Softening Point | 245 °C | 473 °F | B/120; ISO 306 |
| 247 °C | 477 °F | B/50; ISO 306 | |
| UL RTI, Electrical | 130 °C | 266 °F | |
| UL RTI, Mechanical with Impact | 90.0 °C | 194 °F | |
| UL RTI, Mechanical without Impact | 115 °C | 239 °F | |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
|
| Oxygen Index | 29 % | 29 % | ISO 4589 |
| Glow Wire Test | 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Strength | 15.0 kV/mm @Thickness 3.20 mm |
381 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Comparative Tracking Index | 500 V | 500 V | M; IEC 60112 |
| 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 260 - 270 °C | 500 - 518 °F | |
| Zone 2 | 265 - 280 °C | 509 - 536 °F | |
| Zone 3 | 270 - 280 °C | 518 - 536 °F | |
| Melt Temperature | 265 - 280 °C | 509 - 536 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- PolyOne Edgetek® AS-10GF/000 FR V0 BLACK Acrylonitrile Butadiene Styrene (ABS)
- SABIC Innovative Plastics Lexan® FXD104R PC (Asia Pacific)
- PolyOne Elastamax™ XL-0203-12 Styrene Butadiene Block Copolymer (SBC) (discontinued **)
- LyondellBasell Hifaxâ„¢ HSBMG265 Thermoplastic Polyolefin Elastomer
- Shinil Chemical SHINNANO PA-6 Polymer Nanocomposite Engine Cover and Bumper
- Teknor Apex TEKBOND® 6700-55 Thermoplastic Elastomer
- Zircar Zirconia ALF-100 Alumina Felt Insulation
- EMS-Grivory Grivory® BR 40 PA6
- Aclo Accutech Polypropylene Copolymer CP0437W20L1 Wollastonite Reinforced
- Overview of materials for Polypropylene with 40% Talc Filler
Copyright © lookpolymers.com All Rights Reserved