Eurostar Staramide RFM3353EM PA66/6, Glass/Mineral Fiber Reinforced, Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide RFM3353EM PA66/6, Glass/Mineral Fiber Reinforced, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam RFM3353EM is a Mineral Filled, Glass Fiber Reinforced Polyamide 66/ Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Water Absorption | 5.1 % @Temperature 23.0 °C, Time 86400 sec |
5.1 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Moisture Absorption | 1.50 % @Temperature 23.0 °C |
1.50 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Thickness 4.00 mm |
0.0020 - 0.0050 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 115 MPa | 16700 psi | ISO 527 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | 5 mm/min; ISO 527 |
| Flexural Modulus | 8.50 GPa | 1230 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.50 kJ/m² | 2.62 ft-lb/in² | 80x10x4; ISO 179/1eA |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 31.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
17.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C @Thickness 3.20 mm |
482 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Glow Wire Test | 750 °C @Thickness 1.50 mm |
1380 °F @Thickness 0.0591 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | ASTM D527 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | ASTM D527 |
| Comparative Tracking Index | 450 V | 450 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 265 - 275 °C | 509 - 527 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 270 - 280 °C | 518 - 536 °F | |
| Melt Temperature | 270 - 280 °C | 518 - 536 °F | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.15 % | 0.15 % |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Hypalon® HPG-6525 Chlorosulfonated Polyethylene Rubber, Carbon Black Filled Compound &n
- LG Chemical Lupoy 1200HP-15 Polycarbonate Resin
- Zoltek Panex 35® Stitch-Bonded Uni-Directional Carbon Fiber Fabrics
- Arkema Group Lucalor® RB 8067 CPVC, Pipe Grade
- Abatron AboWeld 8104-13 Polysulfide-Epoxy Sealant and Caulk
- AK Steel ASTM A 715 Class 2 Formable, Grade 60F Hot Rolled Carbon Steel, Medium/High Strength Low Alloy (HSLA)
- A. Schulman ComAlloy Hiloy® 616 Nylon 6, Mineral Reinforced
- Abatron AboCast 8502-7/AboCure 8502-7 Colorless, Low-Exotherm Epoxy Casting Compound
- ExxonMobil Mobil Vactra 2
- SABIC Innovative Plastics Lexan® ML1661 PC Copolymer (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved