ATI Wah Chang Tiadyne™ 3510

Category	Metal , Nonferrous Metal , Titanium Alloy
Manufacturer	ATI Wah Chang
Trade Name	Tiadyne™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ATI Wah Chang Tiadyne™ 3510.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Capable of being surface hardened to depths that produce very high wear resistance. Produced by traditional metallurgical processing, not special treatments.Information provided by ATI Wah Chang

Physical Properties	Metric	English	Comments
Density	5.25 g/cc	0.190 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Vickers	250	250	200 g
Tensile Strength, Ultimate	827 MPa	120000 psi	Beta Quenched
	1100 MPa	160000 psi	Fully Hardened
Tensile Strength, Yield	345 MPa	50000 psi	Beta Quenched
	1030 MPa	150000 psi	Fully Hardened
Elongation at Break	12 %	12 %	Fully Hardened
	23 %	23 %	Beta Quenched
Modulus of Elasticity	62.1 GPa	9010 ksi	Beta Quenched
	71.7 GPa	10400 ksi	Fully Hardened

Thermal Properties	Metric	English
CTE, linear	2.34 µm/m-°C @Temperature 500 °C	1.30 µin/in-°F @Temperature 932 °F
	13.7 µm/m-°C @Temperature 100 °C	7.60 µin/in-°F @Temperature 212 °F
Thermal Conductivity	7.58 W/m-K	52.6 BTU-in/hr-ft²-°F
	18.07 W/m-K @Temperature 500 °C	125.4 BTU-in/hr-ft²-°F @Temperature 932 °F

Component Elements Properties	Metric	English
Niobium, Nb (Columbium, Cb)	10.7 - 11.7 %	10.7 - 11.7 %
O2	0.070 - 0.13 %	0.070 - 0.13 %
Titanium, Ti	52.1455 - 55.23 %	52.1455 - 55.23 %
Zirconium, Zr	34 - 36 %	34 - 36 %

Descriptive Properties	Value	Comments
Thermal Diffusivity, cm²/sec	0.033