- Eurostar Staramide R1000IX4 PA66, Impact Modified, Injection Molded
Eurostar Staramide R1000IX4 PA66, Impact Modified, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide R1000IX4 PA66, Impact Modified, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide R1000IX4 is an Impact Modified Polyamide 66 Injection Molding Resin (also known as R1000HI020 Star X 1020)Information provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.011 - 0.015 cm/cm @Time 86400 sec |
0.011 - 0.015 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | ISO 527 |
| Elongation at Break | 70 % | 70 % | ISO 527 |
| Tensile Modulus | 2.20 GPa | 319 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 50.0 MPa | 7250 psi | ISO 178 |
| Flexural Modulus | 1.40 GPa | 203 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 55.0 kJ/m² | 26.2 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 98.0 kJ/m² | 46.6 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 260 - 270 °C | 500 - 518 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 270 - 280 °C | 518 - 536 °F | |
| Melt Temperature | 270 - 280 °C | 518 - 536 °F | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Precision Polymer Engineering S50E Silicone Rubber
- Ravago Manufacturing Americas Hylac® EX28 ABS
- Magyar Aluminum ALO-EL-4F Alumina
- Samsung Cheil Industries Starex® TX-0530T TRABS, Unreinforced
- Sumitomo Chemical ESPOLEX® 4832 Thermoplastic Elastomer
- Tipco Tipcolite® TPF 1317 - Unreinforced Phenolic Resin with Minerals having 42 mm Norton Flow with 9% Hexamine
- Borealis Borstar® MB7542 High Density Polyethylene for Injection Molding
- Fainplast Compounds GA 75/1 Flexible PVC, Flame Retardant Sheathing
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 2.0 PHR Thanecure ZM
- Covestro Apec® DP9-9353 High-Heat Polycarbonate, UV Stabilized (discontinued **)
Copyright © lookpolymers.com All Rights Reserved