Eurostar Staramide P1000J5 PA6, Impact Modified, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer Eurostar Engineering Plastics
Trade Name Staramide
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Staramide P1000J5 PA6, Impact Modified, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Staramide P1000J5 is a Low Temperature Impact Modified, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.017 cm/cm

@Thickness 4.00 mm
 0.017 in/in

@Thickness 0.157 in
 E2P method
Mechanical Properties Metric English Comments
Tensile Strength, Yield 35.0 MPa
5080 psi
50 mm/min; ISO 527
Elongation at Yield 3.7 %
3.7 %
50 mm/min; ISO 527
Tensile Modulus 1.40 GPa
203 ksi
1 mm/min; ISO 527
Flexural Yield Strength 43.0 MPa
6240 psi
2 mm/min; ISO 178
Flexural Modulus 1.20 GPa
174 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 45.0 kJ/m²
21.4 ft-lb/in²
80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80x10x4; ISO 180/1U
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
Flatw 80x10x4, sp=64 mm; ISO 75/Af
Processing Properties Metric English Comments
Zone 1 220 - 230 °C
428 - 446 °F
Zone 2 230 - 240 °C
446 - 464 °F
Zone 3 240 - 250 °C
464 - 482 °F
Melt Temperature 240 - 250 °C
464 - 482 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 75.0 - 85.0 °C

@Time 14400 - 21600 sec
 167 - 185 °F

@Time 4.00 - 6.00 hour
Moisture Content 0.20 %
0.20 %