Eurostar Staramide BS6 PA6, 30% Glass Bead Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide BS6 PA6, 30% Glass Bead Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide BS6 is a 30% Glass Bead Reinforced, Polyamide 6, Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 6.5 % @Temperature 23.0 °C |
6.5 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.015 cm/cm | 0.010 - 0.015 in/in | on Tensile Bar; E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 10 % | 10 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 4.20 GPa | 609 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 108 MPa | 15700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.10 GPa | 595 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80x10x4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
27.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
33.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Vicat Softening Point | 215 °C | 419 °F | B/120; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Oxygen Index | 24 % | 24 % | ISO 4589 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |
| Zone 2 | 240 - 250 °C | 464 - 482 °F | |
| Zone 3 | 240 - 270 °C | 464 - 518 °F | |
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufTech™ GM-3285 PVC Compound
- Flint Hills P4G4K-205 Homopolymer Polypropylene
- Kolon KOPA® KN3311 General Purpose Nylon 66
- Solvay TECHNYL® R AR 130/GF Nylon 66, 30% glass fiber, DRY
- SABIC Innovative Plastics LNP STAT-LOY Cycoloy_CA6200 PC+ABS
- Tipco Tipcolite® TX 321 Phenolic Compound, Wood Flour & Minerals, having Soft Flow & High Electrical Properties
- A. Schulman POLYBATCH™ Blue 4535 Concentrate Based In Polyethylene
- Arkema Group ORGASOL® 2002 D Nat 1 Polyamide 12, Food Contact Approved
- BASF Ultramid® KR 4357 G6 BK 00564 30% Glass Filled PA6/6T (Conditioned)
Copyright © lookpolymers.com All Rights Reserved