Eurostar Star X 1615 33V S4 PA66, Glass Fiber Reinforced, UV stabilized, Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Reinforced, Impact Grade |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Star X |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Star X 1615 33V S4 PA66, Glass Fiber Reinforced, UV stabilized, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Star X 1615 33V S4 is an Impact Modified, Glass Fiber Reinforced, UV stabilized Polyamide 66 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0040 cm/cm @Thickness 4.00 mm |
0.0010 - 0.0040 in/in @Thickness 0.157 in |
E2P method |
| Ash | 33 % @Temperature 650 °C |
33 % @Temperature 1200 °F |
ISO 3451 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 115 MPa | 16700 psi | ISO 527 |
| Elongation at Break | 4.0 - 6.0 % | 4.0 - 6.0 % | |
| Tensile Modulus | 7.30 GPa | 1060 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 |
| Flexural Modulus | 6.10 GPa | 885 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² @Temperature -30.0 °C |
8.57 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1A |
| 30.0 kJ/m² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 85.0 kJ/m² @Temperature -30.0 °C |
40.4 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1U |
| 90.0 kJ/m² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1U | |
| Charpy Impact Unnotched | 9.00 J/cm² | 42.8 ft-lb/in² | Edgew 80x10x4 sp=62; ISO 179/1eU |
| Charpy Impact, Notched | 3.00 J/cm² | 14.3 ft-lb/in² | Edgew 80x10x4 sp=62; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | DSC; ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 260 - 280 °C | 500 - 536 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 270 - 290 °C | 518 - 554 °F | |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP KONDUIT PX08322 PA 6 (Asia Pacific)
- Honeywell ETFE EX30 Mono-Axially Oriented, ETFE Film (discontinued **)
- LG Chemical KEYFLEX BT 1055D Ester Type TPE
- Solvay TECHNYL® A 548B2 V15 PA66, 15% glass fiber, DRY
- Silon TA 2322 HD Blue Catalyst Masterbatch
- Borealis Borclear™ RB707CF Polypropylene Random Copolymer for Blown Film
- Barlog Plastics KEBAFLEX SG 40 A.01 black TPE-S, Shore A40, black
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 440A, Hardened + 316°C Temper
- Covestro Desmopan® 453 Urethane Thermoplastic Elastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved