- Lubrizol Pellethane® 2363-90AE Thermoplastic Polyurethane Elastomer
Lubrizol Pellethane® 2363-90AE Thermoplastic Polyurethane Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | Pellethane® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Pellethane® 2363-90AE Thermoplastic Polyurethane Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0060 cm/cm | 0.0050 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 32 g/10 min @Load 1.20 kg, Temperature 224 °C |
32 g/10 min @Load 2.65 lb, Temperature 435 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 90 | 90 | ASTM D2240 |
| Tensile Strength, Ultimate | 41.3 MPa | 5990 psi | ASTM D412 |
| Elongation at Break | 550 % | 550 % | ASTM D412 |
| 50% Modulus | 0.00660 GPa | 0.957 ksi | ASTM D412 |
| 100% Modulus | 0.0102 GPa | 1.48 ksi | ASTM D412 |
| 300% Modulus | 0.0190 GPa | 2.76 ksi | ASTM D412 |
| Flexural Modulus | 0.0689 GPa | 9.99 ksi | ASTM D790 |
| Tear Strength | 94.6 kN/m | 540 pli | Die C; ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 50 | 50 | H22 Wheel, 1000g; ASTM D1044 |
| Compression Set | 25 % @Temperature 25.0 °C, Time 79200 sec |
25 % @Temperature 77.0 °F, Time 22.0 hour |
ASTM D395, Method B |
| 40 % @Temperature 70.0 °C, Time 79200 sec |
40 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395, Method B | |
| Tensile Set | 60 % | 60 % | Elongation set after break; ASTM D412 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 162 µm/m-°C @Temperature -80.0 - -30.0 °C |
90.0 µin/in-°F @Temperature -112 - -22.0 °F |
ASTM D696 |
| Vicat Softening Point | 89.4 °C | 193 °F | 120°C.hr, 9.8N; ASTM D1525 |
| Glass Transition Temp, Tg | -33.0 °C | -27.4 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 210 °C | 379 - 410 °F | Molding |
| 193 - 210 °C | 379 - 410 °F | Extrusion | |
| Mold Temperature | 16.0 - 60.0 °C | 60.8 - 140 °F | |
| Drying Temperature | 88.0 - 104 °C | 190 - 219 °F |
Users viewing this material also viewed the following:
- Network Polymers Nylon 6030
- Momentive Performance Materials Siloprenâ„¢ LSR 3286/40 Liquid Silicone Rubber - Self-Lubricating / Low Compression Set
- SABIC Innovative Plastics LNP THERMOCOMP LX04015 PEEK (Europe-Africa-Middle East)
- Teknor Apex Flexalloy® 9300-80 Polyvinyl Chloride Elastomer
- Trimay® Wear Plate TWP171 Iron-based Steel Alloy Weld Wire
- ConocoPhillips El Mar® Grade 15W-40 Mid Ash Supreme Oil
- BASF Styropor® BFL 222 EPS
- A. Schulman POLYFORT™ FPP 3711 High Impact Polypropylene
- Overview of materials for Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced
- BASF Ultramid® B3WG5 25% Glass Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved