- Polymer Resources PPX/NY G20 PPO/Nylon 66 Alloy , 20% Glass Reinforced
Polymer Resources PPX/NY G20 PPO/Nylon 66 Alloy , 20% Glass Reinforced
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PPX/NY G20 PPO/Nylon 66 Alloy , 20% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyphenylene Oxide/Nylon 66 Alloy , 20% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 1.0 - 4.0 g/10 min @Load 3.80 kg, Temperature 300 °C |
1.0 - 4.0 g/10 min @Load 8.38 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 114 MPa | 16500 psi | ASTM D638 |
| Tensile Strength, Yield | 114 MPa | 16500 psi | ASTM D638 |
| Flexural Strength | 169 MPa | 24500 psi | ASTM D790 |
| Flexural Modulus | 5.38 GPa | 780 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Temperature 22.8 °C |
0.900 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 268 - 302 °C | 515 - 575 °F | |
| Middle Barrel Temperature | 274 - 302 °C | 525 - 575 °F | |
| Front Barrel Temperature | 279 - 302 °C | 535 - 575 °F | |
| Melt Temperature | 279 - 302 °C | 535 - 575 °F | |
| Mold Temperature | 79.4 - 121 °C | 175 - 250 °F | |
| Drying Temperature | 93.3 - 107 °C | 200 - 225 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.001 |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene® N 3380 GRN Acrylonitrile-Butadiene Rubber
- Lubrizol Advanced Materials PEARLTHANE® 11T80 Thermoplastic Polyurethane Elastomer
- Silon Taborex TA 1135 HD Chemically-Crosslinkable HDPE Compound
- Solvay MIRACARE® MP-24 Surfactant
- Sinotek Materials ZSLG94 High Carbon Graphite
- Borealis Borstar® CB9600 HDPE for Extrusion Coating
- A. Schulman POLYBATCH™ Grey 8218 Concentrate Based In Polyethylene
- Bhansali Engineering Santron IMS 2000 Glitter SAN Resin
- Mitsui MILEX™ XL-1210MB Phenol Aralkyl Resin, Silicone Rubber Modified (discontinued **)
- Samyang Triel® 5500 Thermoplastics Polyetherester Elastomer, General Extrusion
Copyright © lookpolymers.com All Rights Reserved