- DSM Arnite® AV2 370 XL-T PET-GF35
DSM Arnite® AV2 370 XL-T PET-GF35
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 40% Glass Reinforced |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Arnite® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Arnite® AV2 370 XL-T PET-GF35.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
35% Glass Reinforced, Low Outgassing, Thermal conductive material
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ISO 1183 |
| Water Absorption | 0.45 % | 0.45 % | Sim. To ISO 62 |
| Moisture Absorption | 0.180 % | 0.180 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | Sim. To ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | Sim. To ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 150 MPa | 21800 psi | ISO 527-1/-2 |
| Elongation at Break | 1.5 % | 1.5 % | ISO 527-1/-2 |
| Tensile Modulus | 14.0 GPa | 2030 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.750 J/cm² @Temperature 23.0 °C |
3.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ISO 11359-1/-2 |
| Thermal Conductivity | 0.800 W/m-K | 5.55 BTU-in/hr-ft²-°F | through plane; ASTM E1461 |
| 1.65 W/m-K | 11.5 BTU-in/hr-ft²-°F | in plane; ASTM E1461 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.00e+13 ohm-cm | 3.00e+13 ohm-cm | IEC 60093 |
| Dielectric Constant | 14 @Frequency 1.00e+9 Hz |
14 @Frequency 1.00e+9 Hz |
IEC60250 |
| 23 @Frequency 1.00e+6 Hz, Temperature 23.0 °C |
23 @Frequency 1.00e+6 Hz, Temperature 73.4 °F |
||
| 50 @Frequency 10000 Hz, Temperature 23.0 °C |
50 @Frequency 10000 Hz, Temperature 73.4 °F |
||
| 70 @Frequency 100 Hz, Temperature 23.0 °C |
70 @Frequency 100 Hz, Temperature 73.4 °F |
||
| 125 @Frequency 1.00 Hz, Temperature 23.0 °C |
125 @Frequency 1.00 Hz, Temperature 73.4 °F |
||
| Dielectric Strength | 1.10 kV/mm | 27.9 kV/in | IEC 60243-1 |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers AvaSpire® AV-848 GF30 Polyaryletherketone (PAEK) (Unverified Data**)
- Overview of materials for Polycarbonate/ABS Alloy, Carbon Fiber Filled
- MarkeTech Gadolinium silicate:Cerium (GSO:Ce; Gd2SiO5) Scintillator Crystal
- Momentive Performance Materials RTV6186 Clear Potting/Encapsulating Gel
- Struktol VM 512 LUBRICANT ADDITIVE FOR PVC AND POLYMER PROCESSING
- ChevronTexaco Tool Joint Compound
- Arkema Group EVATANE® 33-45 Copolymer Ethylene - Vinyl Acetate
- Aclo Acculoy POL062L Polycarbonate PET Alloy
- Advanced Polymer Alloys Alcryn® 4660 BK Melt Processable Rubber
- Haynes 230® alloy, cold rolled and 1232°C solution annealed sheet
Copyright © lookpolymers.com All Rights Reserved