Eastman Neostar FN007 Elastomer

Category	Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP
Manufacturer	Eastman Chemical
Trade Name	Neostar
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Eastman Neostar FN007 Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Neostar FN007 elastomer is the third in Eastman’s series of tough, clear, durable copolyester ethers. Though originally designed for use in the profile and automotive markets, this innovative copolymer has also found use in tubing and packaging applications. Its excellent chemical, heat, and puncture resistance combined with its strength and durability make it a good choice for applications that require flex-crack resistance and a general utility in harsh environments. Neostar FN007 can be injection molded, extruded in blown film or tubing, or extrusion blow molded. The target inherent viscosity of this product is 1.23.Applications/UsesAutomotiveFlexible hingesPricing channelsRetail pricing finsDriver and passenger side air bagsPackagingProfilesTubingKey AttributesEnvironmentally preferred, non-halogenated materialExcellent chemical resistanceExceptional heat resistance and high temperature dimensional stabilityHigh flexibility without plasticizersSolvent bondable

Physical Properties	Metric	English	Comments
Specific Gravity	1.13 g/cc	1.13 g/cc	ASTM D792
Water Absorption	0.40 %	0.40 %	24h Immersion; ASTM D570
Viscosity Measurement	1.23	1.23	Inherent; EMN-A-AC-G-V-1
Melt Flow	4.0 g/10 min @Load 2.16 kg, Temperature 230 °C	4.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	95	95	ASTM D2240
Hardness, Shore D	55	55	ASTM D2240
Tensile Strength at Break	23.0 MPa	3340 psi	ASTM D638
Tensile Strength, Yield	13.0 MPa	1890 psi	ASTM D638
Elongation at Break	400 %	400 %	ASTM D638
Elongation at Yield	38 %	38 %	ASTM D638
Tensile Modulus	0.170 GPa	24.7 ksi	ASTM D638
Flexural Modulus	0.150 GPa	21.8 ksi	ASTM D790
Izod Impact, Notched	0.400 J/cm @Temperature -40.0 °C	0.749 ft-lb/in @Temperature -40.0 °F	ASTM D256
Tear Strength, Total	350 N	78.7 lb (f)	ASTM D1004

Thermal Properties	Metric	English	Comments
Heat of Fusion	27.0 J/g	11.6 BTU/lb	ASTM E793
CTE, linear	150 µm/m-°C @Temperature 20.0 °C	83.3 µin/in-°F @Temperature 68.0 °F	ASTM D696
Specific Heat Capacity	1.60 J/g-°C	0.382 BTU/lb-°F	DSC
	1.80 J/g-°C @Temperature 100 °C	0.430 BTU/lb-°F @Temperature 212 °F	DSC
	2.00 J/g-°C @Temperature 150 °C	0.478 BTU/lb-°F @Temperature 302 °F	DSC
	2.30 J/g-°C @Temperature 175 °C	0.550 BTU/lb-°F @Temperature 347 °F	solid; DSC
	2.30 J/g-°C @Temperature 225 °C	0.550 BTU/lb-°F @Temperature 437 °F	melt; DSC
	3.10 J/g-°C @Temperature 200 °C	0.741 BTU/lb-°F @Temperature 392 °F	transition; DSC
Thermal Conductivity	0.190 W/m-K	1.32 BTU-in/hr-ft²-°F	ASTM C177
Melting Point	205 °C	401 °F	Crystalline Peak Melting Point; ASTM D3418
Crystallization Temperature	140 °C	284 °F	on cooling; DSC
Vicat Softening Point	170 °C	338 °F	1kg load; ASTM D1525
Brittleness Temperature	<= -75.0 °C	<= -103 °F	ASTM D746
Glass Transition Temp, Tg	-3.00 °C	26.6 °F	DSC
Clash Berg Stiffness Temperature	<= -70.0 °C	<= -94.0 °F	at 930 MPa; ASTM D1043
	-28.0 °C	-18.4 °F	at 240 MPa; ASTM D1043