PolyOne Stat-Tech™ PC-CB2/000 CR Polycarbonate (PC)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Stat-Tech™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Stat-Tech™ PC-CB2/000 CR Polycarbonate (PC).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Stat-Tech™ PC-CB2/000 CR XP100827Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 - 1.23 g/cc | 1.19 - 1.23 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.2 - 72.4 MPa | 8010 - 10500 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 3.0 - 7.0 % | 3.0 - 7.0 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.07 - 3.45 GPa | 300 - 500 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 89.6 - 103 MPa | 13000 - 14900 psi | ASTM D790 |
| Flexural Modulus | 1.72 - 3.10 GPa | 249 - 450 ksi | ASTM D790 |
| Izod Impact, Notched | 0.370 - 0.530 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.693 - 0.993 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.18 mm |
253 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C | 234 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 - 10000 ohm-cm | 100 - 10000 ohm-cm | ASTM D257 |
| Surface Resistance | 1000 ohm - 1e+05 | 1000 ohm - 1e+05 | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 300 - 320 °C | 572 - 608 °F | |
| Mold Temperature | 90.0 - 110 °C | 194 - 230 °F | |
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Clean/High Purity | |
| Electrically Conductive | ||
| Filler / Reinforcement | Carbon Nano Filler | |
| Forms | Pellets | |
| Generic Material | PC | |
| Generic Name | Polycarbonate (PC) | |
| Processing Method | Injection Molding | |
| Regional Availability | Asia Pacific | |
| Uses | Aerospace Applications | |
| Automotive Electronics | ||
| Business Equipment | ||
| Computer Components | ||
| Connectors | ||
| Electrical Housing | ||
| Electrical/Electronic Applications | ||
| Housings |
Users viewing this material also viewed the following:
- Multibase SILASTIC® C7-4550 DICUP R Dow-Corning Biomedical Grade ETR Elastomer
- SABIC PS 160 General Purpose Polystyrene for Foam Extrusion
- ExxonMobil Vyram™ 9103-54 Thermoplastic Elastomer (discontinued **)
- Sylvin Technologies 9999-70 Natural PVC Molding Compound
- SABIC Innovative Plastics LNP THERMOCOMP OF008AH PPS - Branched
- SABIC Innovative Plastics Valox® V2000DM PBT
- Sax Polymers SAXLAC 320A Acrylonitrile Butadiene Styrene
- ThyssenKrupp XAR® 400 Structural Steel
- A. Schulman POLYFORT™ FPP 1285U Glass Filled, UV Stable Impact Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved