EMS-Grivory Grivory® XE 4155 black 9992 PA612-I
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® XE 4155 black 9992 PA612-I.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 |
| Water Absorption | 2.3 % | 2.3 % | ISO 62 |
| Moisture Absorption | 1.00 % | 1.00 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 68 | 68 | conditioned, 15s; ISO 868 |
| 72 | 72 | dry, 15s; ISO 868 | |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | dry; ISO 527-1/-2 |
| 40.0 MPa | 5800 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | >= 50 % | >= 50 % | dry; ISO 527-1/-2 |
| >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | |
| Elongation at Yield | 5.0 % | 5.0 % | dry; ISO 527-1/-2 |
| 20 % | 20 % | conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 0.950 GPa | 138 ksi | conditioned; ISO 527-1/-2 |
| 1.50 GPa | 218 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | NB | NB | dry; ISO 179/1eU |
| NB | NB | conditioned; ISO 179/1eU | |
| NB @Temperature 30.0 °C |
NB @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| NB @Temperature 30.0 °C |
NB @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 7.50 J/cm² | 35.7 ft-lb/in² | dry; ISO 179/1eA |
| NB | NB | conditioned; ISO 179/1eA | |
| 2.00 J/cm² @Temperature 30.0 °C |
9.52 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 2.00 J/cm² @Temperature 30.0 °C |
9.52 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 180 µm/m-°C | 100 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 213 °C | 415 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | conditioned; IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Strength | 37.0 kV/mm | 940 kV/in | dry; IEC 60243-1 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive | Air intake sytems | |
| Automotive electr. and electronics, lighting | ||
| Compressed air systems | ||
| Cooling and climate control | ||
| Hydraulic systems | ||
| Electricals & Electronics | Cables & Tubes | |
| Form | Granules | |
| Industry & Consumer goods | Hydraulics & Pneumatics | |
| Processing | Other Extrusion | |
| Profile Extrusion | ||
| Product Attributes | High viscosity | |
| Hydrolysis resistant | ||
| Special Characteristics | High impact or impact modified | |
| Improved heat resistance |
Users viewing this material also viewed the following:
- PolyOne LubriOne™ NN-30GF/13T-2S Black Polyamide 66 (Nylon 66)
- DuPont™ Sclairfilm® MPP-1 LLDPE Film, "Super Strength", 25 µm Thickness (discontinued **)
- Hong Kun Group 2,6-Dibromotoluene Pharmaceutical Intermediate
- Kazanorgsintez 108-277 Low Density Polyethylene Composition with Improved Processibility
- Taiwan PU Corporation TPUI-ED64 General Grade, Injection Molding Polyester Base TPU
- SABIC Innovative Plastics LNP THERMOCOMP UF006H PPA
- DuPont Elvaloy® 742 Ethylene/Vinyl Acetate/Carbon Monoxide Copolymer
- Eurostar Staramide 6 80E7 PA6, Injection Molded
- A. Schulman ComAlloy Lubrilon® 629 Nylon 6/6, Glass Fiber/PTFE Filled, Flow Enhanced
- Axiall 38831 Coax & Telecom Flexible PVC
Copyright © lookpolymers.com All Rights Reserved