Garlock GYLONÂ® 3510 PTFE Gasketing, Barium Sulfate Filler

Category	Polymer , Thermoplastic , Fluoropolymer , PTFE
Manufacturer	Garlock Rubber Technologies
Trade Name	GYLON®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Garlock GYLONÂ® 3510 PTFE Gasketing, Barium Sulfate Filler.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PTFE with barium sulfate filler.Improved sealing performance over conventional PTFEUnique manufacturing process minimizes cold flow problems typical of skived and expanded PTFE sheetsExcellent bolt torque retentionWithstands a wide range of chemicals for extended service lifeMedia: Strong caustics, Moderate acids, Chlorine, Gases, Water, Steam, Hydrocarbons, Cryogenics and aluminum fluorideInformation provided by Garlock Rubber Technologies

Physical Properties	Metric	English	Comments
Permeability	0.015	0.015	Gas Permeability, cc/min; DIN 3535 Part 4

Mechanical Properties	Metric	English	Comments
Tensile Strength	13.8 MPa	2000 psi	across grain; ASTM F152

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	260 Â°C @Pressure 8.27 MPa	500 Â°F @Pressure 1200 psi	Continuous
Minimum Service Temperature, Air	-268 Â°C	-450 Â°F

Electrical Properties	Metric	English	Comments
Dielectric Strength	>= 18.3 kV/mm @Temperature 121 Â°C, Time 10800 sec	>= 466 kV/in @Temperature 250 Â°F, Time 3.00 hour	0.0625 in. thickness; ASTM D149
	2.32 kV/mm @Thickness 1.59 mm	59.0 kV/in @Thickness 0.0625 in	100% RH for 96 hours; ASTM D149

Descriptive Properties	Value	Comments
Color	Off-White
Compressibility, %	4-10	ASTM F36
Creep Relaxation, %	11	ASTM F38
Sealability ASTM F37B, ml/hr	0.04	ASTM Fuel A