EMS-Grivory Grivory® TSG-35 PA666-GF35
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 40% Glass Fiber Reinforced |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® TSG-35 PA666-GF35.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Water Absorption | 6.0 % | 6.0 % | ISO 62 |
| Moisture Absorption | 2.00 % | 2.00 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 100 MPa | 14500 psi | conditioned; ISO 2039-1 |
| 220 MPa | 31900 psi | dry; ISO 2039-1 | |
| Tensile Strength at Break | 130 MPa | 18900 psi | conditioned; ISO 527-1/-2 |
| 225 MPa | 32600 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | dry; ISO 527-1/-2 |
| 6.0 % | 6.0 % | conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 6.50 GPa | 943 ksi | conditioned; ISO 527-1/-2 |
| 11.0 GPa | 1600 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 8.50 J/cm² | 40.4 ft-lb/in² | dry; ISO 179/1eU |
| 9.00 J/cm² | 42.8 ft-lb/in² | conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | dry; ISO 179/1eA |
| 2.50 J/cm² | 11.9 ft-lb/in² | conditioned; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 100 - 120 °C | 212 - 248 °F | long term; EMS |
| 180 °C | 356 °F | short term; EMS | |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 160 °C | 320 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | conditioned; IEC 60093 |
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Strength | 21.0 kV/mm | 533 kV/in | conditioned; IEC 60243-1 |
| 26.0 kV/mm | 660 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 500 V | 500 V | conditioned; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive | Air intake sytems | |
| Powertrain and Chassis | ||
| Electricals & Electronics | Electrical appliances | |
| Electrical equipment | ||
| Form | Granules | |
| Industry & Consumer goods | Housewares | |
| Mechanical Engineering | ||
| Sports & Leisure | ||
| Tools & Accessories | ||
| Processing | Injection Molding |
Users viewing this material also viewed the following:
- Multibase TPSiV® 3111-70A Thermoplastic Elastomer
- ND Industries SuperGlue Ethyl 316
- Polimeri Europa Clearflex® CL B0 Very Low Density Polyethylene
- Lehmann & Voss LUVOCOM® 1105-7781/BK PEEK, with carbon fiber
- Kolon KOPA® KN163G30 G/F Reinforced Nylon 6
- Iran Petrochemical (PCC) 5030UA High Density Polyethylene
- A. Schulman POLYBATCH™ Mahogany 50381 Concentrate Based in Polyethylene
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 10.0 PHR Plasthall 7050 Plasticizer
- 3M FM016 Indoor UL Recognized Clear Polyester Overlaminate Label Product
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 410, Hardened + 538°C Temper
Copyright © lookpolymers.com All Rights Reserved