EMS-Grivory Grivory® BGZ-50/2 PA6-I-GF50
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® BGZ-50/2 PA6-I-GF50.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ISO 1183 |
| Water Absorption | 5.0 % | 5.0 % | ISO 62 |
| Moisture Absorption | 1.50 % | 1.50 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 170 MPa | 24700 psi | conditioned; ISO 2039-1 |
| 280 MPa | 40600 psi | dry; ISO 2039-1 | |
| Tensile Strength at Break | 150 MPa | 21800 psi | conditioned; ISO 527-1/-2 |
| 230 MPa | 33400 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | dry; ISO 527-1/-2 |
| 6.0 % | 6.0 % | conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 10.0 GPa | 1450 ksi | conditioned; ISO 527-1/-2 |
| 16.0 GPa | 2320 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 9.50 J/cm² | 45.2 ft-lb/in² | dry; ISO 179/1eU |
| 13.0 J/cm² | 61.9 ft-lb/in² | conditioned; ISO 179/1eU | |
| 9.00 J/cm² @Temperature 30.0 °C |
42.8 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 9.50 J/cm² @Temperature 30.0 °C |
45.2 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | dry; ISO 179/1eA |
| 2.50 J/cm² | 11.9 ft-lb/in² | conditioned; ISO 179/1eA | |
| 1.10 J/cm² @Temperature 30.0 °C |
5.23 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 1.20 J/cm² @Temperature 30.0 °C |
5.71 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C | 8.33 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 100 - 120 °C | 212 - 248 °F | long term; EMS |
| 180 °C | 356 °F | short term; EMS | |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 165 °C | 329 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | conditioned; IEC 60093 |
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Strength | 38.0 kV/mm | 965 kV/in | conditioned; IEC 60243-1 |
| 41.0 kV/mm | 1040 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 550 V | 550 V | conditioned; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Granules | |
| Processing | Injection Molding | |
| Special Characteristics | High impact or impact modified |
Users viewing this material also viewed the following:
- ExxonMobil Vyram™ 9101-75 Thermoplastic Elastomer (discontinued **)
- Nilit FRIANYL B63 HS-GV35 Nylon 6 for injection molding, 35% glass fiber reinforced
- Polyram Polytron A30N02 Nylon 66, 30% Long Fiber
- Wieland 1602 Wilaform Gold
- Dow Corning SYL-OFF® PMCPSL 400 Coating
- ExxonMobil Metallyte™ 18MM488 OPP Film
- Arkema Group OREVAC® 18319 Grafted Maleic Anhydride Polyethylene
- Buckeye Polymers BP PPC 0510-20 BLK Polypropylene Copolymer
- DuPont Performance Polymers Delrin® SC631 NC010 Acetal (POM) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved