Cossa Polimeri ESTACARB 0820 GF Polycarbonate, 10% Glass Filled
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTACARB |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTACARB 0820 GF Polycarbonate, 10% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate with 10% glass fiber reinforcementHigh stiffness, good impact resistanceInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D 955 |
| Melt Flow | 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D 638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D 638 |
| Flexural Modulus | 3.60 GPa | 522 ksi | ASTM D 790 |
| Izod Impact, Notched | 1.00 J/cm @Temperature 0.000 °C |
1.87 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 |
| 1.20 J/cm @Temperature 23.0 °C |
2.25 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 135 °C | 275 °F | I.E.C. 335-1 |
| Vicat Softening Point | 144 °C @Load 5.00 kg |
291 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| 150 °C @Load 0.999 kg |
302 °F @Load 2.20 lb |
50°C/hr; ASTM D 1525 | |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
||
| Glow Wire Test | 850 °C @Thickness 2.00 mm |
1560 °F @Thickness 0.0787 in |
I.E.C. 695-2-1 |
Users viewing this material also viewed the following:
- Omnia Plastica PVDF Kynar
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR Mistron Vapor Filler
- Karina Polyethylene Based Anti UV MB
- Lehmann & Voss LUVOCOM® 21-7928 Polyamide 6/6T, with carbon fiber, lubricant modified
- TIMCAL TIMREX® T15-75 Primary Synthetic Graphite
- A. Schulman POLYBATCH™ Blue 40395U Concentrate Based In LLDPE
- ChevronTexaco Vanguard® 680
- ExxonMobil LD 617.LN Molding, Extrusion and Compounding Resin
- Arkema Group Rilsan® AMN P20 TLD Nylon 12, Flexible, Injection Grade (Dry)
- Seals Eastern 5403 Nitrile Rubber
Copyright © lookpolymers.com All Rights Reserved