E-Polymers TEKAMID® TA210G15 , 15% Glass Fiber Reinforced PA66, DAM
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | E-Polymers Co. Ltd. |
| Trade Name | TEKAMID® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | E-Polymers TEKAMID® TA210G15 , 15% Glass Fiber Reinforced PA66, DAM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Beautiful surface, strength propertyInformation provided by E-Polymers Co. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | 23°C/24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D786 |
| Tensile Strength, Yield | 130 MPa | 18900 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Yield Strength | 180 MPa | 26100 psi | ASTM D790 |
| Flexural Modulus | 5.00 GPa | 725 ksi | ASTM D790 |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 60.0 J/cm @Thickness 3.20 mm |
112 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C @Temperature 20.0 °C |
22.2 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Melting Point | 260 °C | 500 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F |
Users viewing this material also viewed the following:
- Asahi Kasei Tenac® LA531 Acetal Homopolymer, High Lubricity (discontinued **)
- Lucas-Milhaupt BRAZE 630 Silver Based Cadmium Free Filler Metal
- Styrolution Terblend® N NM-11 ABS/PA6 (Conditioned)
- Chase Plastics CP Pryme® N100M2 (Dry) Nylon 6, Lubricated
- Aclo Accutech Polypropylene Homopolymer HP0339W20L Wollastonite Reinforced
- Zeon Chemicals Nipol® N917 Nitrile Elastomer
- Polymer Resources AC-GP1 Acetal Copolymer, Low Flow, High Melt Strength (Unverified Data**)
- Arkema Group Oroglas® VS-UVT Acrylic, Injection Molding Grade (discontinued **)
- SMAC CABLE® 2516S-10-10 Damping Material
Copyright © lookpolymers.com All Rights Reserved