A. Schulman POLYPUR™ FPU 1152C Thermoplastic Polyurethane

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded , Polyurethane, TP
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman POLYPUR™ FPU 1152C Thermoplastic Polyurethane.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by A. Schulman.
Physical Properties Metric English Comments
Specific Gravity 1.27 g/cc
1.27 g/cc
ASTM D792
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
 0.0010 - 0.0030 in/in

@Thickness 0.126 in
 48 hr, at 80 and 121°C; ASTM D955
0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
 0.0010 - 0.0030 in/in

@Thickness 0.126 in
 72 hr; ASTM D955
Mechanical Properties Metric English Comments
Hardness, Shore D 56
56
15 sec delay; ASTM D2240
Tensile Strength, Ultimate 31.0 MPa
4500 psi
2 in/min, at max load; ASTM D638
Tensile Strength, Yield 26.0 MPa
3770 psi
2 in/min; ASTM D638
Elongation at Break 400 %
400 %
ASTM D412
Flexural Modulus 0.750 GPa
109 ksi
1.3 mm/min; ASTM D790
Izod Impact, Notched 5.00 J/cm
9.37 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 20.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 11.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM E831
Deflection Temperature at 0.46 MPa (66 psi) 75.0 °C
167 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 53.0 °C
127 °F
ASTM D648