- Covestro Makroblend® DP 2-7655 Polycarbonate + PET, Mineral Filled Impact Grade
Covestro Makroblend® DP 2-7655 Polycarbonate + PET, Mineral Filled Impact Grade
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Covestro |
| Trade Name | Makroblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Covestro Makroblend® DP 2-7655 Polycarbonate + PET, Mineral Filled Impact Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Developmental productISO 7792-1-PC/PET,MHPR,-030,MD10(PC+PET)-blendsimpact modifiedInjection molding grade 10% mineral filledPreprocessingMax. Water content
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| 1.11 g/cc @Temperature 270 °C |
0.0401 lb/in³ @Temperature 518 °F |
Melt | |
| Water Absorption | 0.90 % | 0.90 % | Similar to ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | Similar to ISO 62 |
| Melt Flow | 11 g/10 min @Load 5.00 kg, Temperature 260 °C |
11 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527-1/-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | ISO 11359-1/-2 |
| Specific Heat Capacity | 1.71 J/g-°C | 0.409 BTU/lb-°F | Melt |
| Thermal Conductivity | 0.196 W/m-K | 1.36 BTU-in/hr-ft²-°F | Melt |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 111 °C | 232 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
IEC 60695-11-10 | |
| Oxygen Index | 23 % | 23 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.5 @Frequency 100 Hz |
3.5 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 36.0 kV/mm | 914 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0038 @Frequency 100 Hz |
0.0038 @Frequency 100 Hz |
IEC 60250 |
| 0.019 @Frequency 1.00e+6 Hz |
0.019 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| 270 °C | 518 °F | Injection Molding; ISO 294 | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| 70.0 °C | 158 °F | Injection Molding; ISO 10724 | |
| Ejection Temperature | 170 °C | 338 °F | |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America | ||
| Eff. thermal diffusivity (m²/s) | 1.04E-07 | |
| Feature | Release agent | |
| Form | Pellets | |
| Process | Injection Molding |
Users viewing this material also viewed the following:
- Plansee Ta2.5W Tantalum-Tungsten 2.5 Alloy
- SABIC Innovative Plastics Lexan® FXD123R PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics Lexan® SLX2231T PC Copolymer
- Lucite International Colacryl ® TS 1649 Acrylic Orthodontic Polymer
- Fiberfil® J-60/15/MI/20 Polypropylene Homopolymer, 35% Glass/mica Reinforced
- Eurostar Starflam PX06020 PA6, Flame Retardant, Injection Molded
- Indium Corp. Indalloy 203 Indium Solder Alloy
Copyright © lookpolymers.com All Rights Reserved