SABIC Innovative Plastics LNP LUBRICOMP RCL36S PA 66 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RCL36S PA 66 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* RCL36S is a compound based on Nylon 66 resin containing Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.530 % | 0.530 % | 50% RH, 24 hrs; ASTM D570 |
| 0.840 % | 0.840 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0011 cm/cm @Time 86400 sec |
0.0011 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0072 cm/cm @Time 86400 sec |
0.0072 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 182 MPa | 26400 psi | ASTM D638 |
| 245 MPa | 35500 psi | ISO 527 | |
| Elongation at Break | 0.90 % | 0.90 % | ASTM D638 |
| 1.8 % | 1.8 % | ISO 527 | |
| Tensile Modulus | 22.6 GPa | 3280 ksi | 1 mm/min; ISO 527 |
| 32.4 GPa | 4700 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 372 MPa | 54000 psi | ASTM D790 |
| 395 MPa | 57300 psi | ISO 178 | |
| Flexural Modulus | 18.4 GPa | 2670 ksi | ASTM D790 |
| 22.7 GPa | 3290 ksi | ISO 178 | |
| Izod Impact, Notched | 1.01 J/cm | 1.89 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.46 J/cm | 19.60 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 68.0 kJ/m² | 32.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J | 7.38 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.36 | 0.36 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.30 | 0.30 | ASTM D3702 Modified |
| K (wear) Factor | 30.2 x 10-8 mm³/N-M | 15.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | >= 240 °C | >= 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 255 °C @Thickness 3.20 mm |
491 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs SM100 Sm(C2H3O2)3·3H2O Samarium acetate hydrate
- Oceanchem Group Decabromodiphenyl Ethane (DBDPE/8010)
- Total Finaprene® 602 Styrene-Butadiene TPE Copolymer Compound, Formulated to 61 Shore A (discontinued **)
- Polyram PlusTek PA823M6 Nylon 6.6 for Injection Molding, 30% Minerals Reinforced, Impact Modified
- Master Bond EP30M4 Chemically Resistant Two Component Epoxy System
- A. Schulman POLYTROPE™ TPP 620 Olefinic Elastomer
- Elektro-Isola Etronax MF Phenolic, Cotton Fabric Reinforcement, Brown, Sheets
- DuPont Performance Polymers Zytel® RS LC1000 BK385 Nylon 1010
- ExxonMobil Mobil Rarus 1024 SHC 1000 Series
Copyright © lookpolymers.com All Rights Reserved