DuPont Performance Polymers Rynite® FR531 NC010 Polyethylene Terephthalate (PET) (Unverified Data**)
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Rynite® FR531 NC010 Polyethylene Terephthalate (PET)
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
36% Reinforced Flame Retardant Polyethylene Terephthalate Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.83 g/cc | 0.0661 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4 2577 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4 2577 |
| Melt Flow | 3.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
3.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
cm³/10min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 129 MPa | 18700 psi | ISO 527-1/-2 |
| Elongation at Break | 1.6 % | 1.6 % | ISO 527-1/-2 |
| Tensile Modulus | 12.6 GPa | 1830 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 3.60 J/cm² | 17.1 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 247 °C | 477 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
IEC 60695-11-10 |
| V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
IEC 60695-11-10 | |
| 5VA @Thickness 2.00 mm |
5VA @Thickness 0.0787 in |
IEC 60695-11-20 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 325 V | 325 V | IEC 60112 |
| 250 - 400 V | 250 - 400 V | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Delivery Form | Pellets | |
| Processing | Injection Moulding | |
| Regional Availability | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| UL recognition | UL |
Users viewing this material also viewed the following:
- Polimeri Europa Dutral® CO 043 Ethylene - Propylene
- Quadrant EPP Semitron® ESd 520HR PAI, static dissipative, extruded (ISO Data)
- Resin Technology Group 390 Surface Insensitive Fusion™ Cyanoacrylate Instant Ethyl Adhesive
- SABIC Innovative Plastics Lexan® LUX2614G PC (Europe-Africa-Middle East)
- Kinlead PL11 Lamination Grade BOPP Plain Film (thickness: 18 µm)
- Taiwan Sheen Soon Sheenthane® A8600F Thermoplastic Polyurethane Elastomer
- Special Metals MONEL® Alloy 400
- CP-Polymer-Technik Wellamid® 6000 GS 50 HWCP 50% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry
- ATI Allegheny Ludlum AL 13-8™ H 950 Precipitation Hardening Alloy
- BASF Ultramid® B3GM35 BK 60564 40% Glass/Mineral Filled PA6 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved