PTS Tristar® PC-20GFR 20% Glass Reinforced Polycarbonate With Release
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Tristar® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Tristar® PC-20GFR 20% Glass Reinforced Polycarbonate With Release.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Water Absorption | 0.12 % | 0.12 % | 24 hours at 73°F; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 110.3 MPa @Thickness 3.17 mm |
16000 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 5.0 % @Thickness 3.17 mm |
5.0 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Yield Strength | 131 MPa @Thickness 3.17 mm |
19000 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 5.38 GPa @Thickness 3.17 mm |
780 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm |
2.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | ASTM D648 |
| UL RTI, Electrical | 80.0 °C | 176 °F | |
| 80.0 °C | 176 °F | ||
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | |
| 80.0 °C | 176 °F | ||
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | |
| 80.0 °C | 176 °F | ||
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
|
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | PLC 6 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | PLC 4 |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | PLC 1 |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | PLC 0 |
Users viewing this material also viewed the following:
- Overview of materials for Acrylonitrile Butadiene Styrene (ABS), NCG Fiber Filled
- LG Chemical HI835S PMMA, Impact Resistant Grade
- Lanxess Pocan® BF 4130 XF 700051 PBT, 30% Glass Fiber
- A. Schulman POLYBATCH™ Deep Red 50389 Concentrate Based In Linear Low-Density Polyethylene
- A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black
- Dow Corning FOX® PMCP16 Flowable Oxide
- Diamond Polymers NYLON 6615 Black, Super Tough
- Carpenter Hiperco® 50 Fe-Co-V Soft Magnetic Alloy, 0.15 mm Strip Heat Treated 843°C
- Ashley Polymers Ashlene® 830L-13G Nylon 6, 13% Glass Reinforced
- Beijing Chemical Industry KAIFA® MN301-G20 Nylon 66 Resin
Copyright © lookpolymers.com All Rights Reserved