DuPont Performance Polymers Delrin® FG500P NC010 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® FG500P NC010 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Medium Viscosity Acetal Homopolymer Developed for Food Contact Applications Delrin FG500P is a medium viscosity acetal homopolymer with improved thermal stability. It has been developed for consideration into applications such as parts for the food indInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 1.4 %

@Thickness 2.00 mm
 1.4 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.300 %

@Thickness 2.00 mm
 0.300 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 92857 cP

@Shear Rate 5000 1/s,
Temperature 230 °C
 92857 cP

@Shear Rate 5000 1/s,
Temperature 446 °F
 ISO 11403-1 -2
100600 cP

@Shear Rate 5000 1/s,
Temperature 215 °C
 100600 cP

@Shear Rate 5000 1/s,
Temperature 419 °F
 ISO 11403-1 -2
107100 cP

@Shear Rate 5000 1/s,
Temperature 200 °C
 107100 cP

@Shear Rate 5000 1/s,
Temperature 392 °F
 ISO 11403-1 -2
260530 cP

@Shear Rate 500 1/s,
Temperature 230 °C
 260530 cP

@Shear Rate 500 1/s,
Temperature 446 °F
 ISO 11403-1 -2
298700 cP

@Shear Rate 500 1/s,
Temperature 215 °C
 298700 cP

@Shear Rate 500 1/s,
Temperature 419 °F
 ISO 11403-1 -2
348640 cP

@Shear Rate 500 1/s,
Temperature 200 °C
 348640 cP

@Shear Rate 500 1/s,
Temperature 392 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.020 cm/cm
0.020 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.019 cm/cm
0.019 in/in
ISO 294-4 2577
Melt Flow 13 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 13 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 cm³/10min; ISO 1133
15 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 15 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 92
92
ISO 2039-2
Hardness, Rockwell R 120
120
ISO 2039-2
Tensile Stress 20.0 MPa

@Strain 0.476 %,
Temperature -40.0 °C
 2900 psi

@Strain 0.476 %,
Temperature -40.0 °F
 ISO 11403-1 -2
20.0 MPa

@Strain 0.527 %,
Temperature -20.0 °C
 2900 psi

@Strain 0.527 %,
Temperature -4.00 °F
 ISO 11403-1 -2
26.5 MPa

@Strain 1.20 %,
Temperature 40.0 °C
 3840 psi

@Strain 1.20 %,
Temperature 104 °F
 ISO 11403-1 -2
30.9 MPa

@Strain 1.10 %,
Temperature 23.0 °C
 4480 psi

@Strain 1.10 %,
Temperature 73.4 °F
 ISO 11403-1 -2
41.0 MPa

@Strain 1.30 %,
Temperature 0.000 °C
 5950 psi

@Strain 1.30 %,
Temperature 32.0 °F
 ISO 11403-1 -2
53.4 MPa

@Strain 4.80 %,
Temperature 40.0 °C
 7750 psi

@Strain 4.80 %,
Temperature 104 °F
 ISO 11403-1 -2
58.3 MPa

@Strain 8.30 %,
Temperature 40.0 °C
 8460 psi

@Strain 8.30 %,
Temperature 104 °F
 ISO 11403-1 -2
60.3 MPa

@Strain 4.40 %,
Temperature 23.0 °C
 8750 psi

@Strain 4.40 %,
Temperature 73.4 °F
 ISO 11403-1 -2
65.9 MPa

@Strain 7.80 %,
Temperature 23.0 °C
 9560 psi

@Strain 7.80 %,
Temperature 73.4 °F
 ISO 11403-1 -2
71.5 MPa

@Strain 5.30 %,
Temperature 0.000 °C
 10400 psi

@Strain 5.30 %,
Temperature 32.0 °F
 ISO 11403-1 -2
74.93 MPa

@Strain 4.50 %,
Temperature -20.0 °C
 10870 psi

@Strain 4.50 %,
Temperature -4.00 °F
 ISO 11403-1 -2
75.5 MPa

@Strain 9.30 %,
Temperature 0.000 °C
 11000 psi

@Strain 9.30 %,
Temperature 32.0 °F
 ISO 11403-1 -2
80.0 MPa

@Strain 3.81 %,
Temperature -40.0 °C
 11600 psi

@Strain 3.81 %,
Temperature -40.0 °F
 ISO 11403-1 -2
82.32 MPa

@Strain 9.00 %,
Temperature -20.0 °C
 11940 psi

@Strain 9.00 %,
Temperature -4.00 °F
 ISO 11403-1 -2
96.5 MPa

@Strain 12.0 %,
Temperature -40.0 °C
 14000 psi

@Strain 12.0 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Tensile Strength, Yield 70.0 MPa
10200 psi
ISO 527-1/-2
Elongation at Break 30 %
30 %
Nominal; ISO 527-1/-2
Elongation at Yield 17 %
17 %
ISO 527-1/-2
Tensile Modulus 3.10 GPa
450 ksi
ISO 527-1/-2
Flexural Strength 80.0 MPa

@Strain 3.50 %
 11600 psi

@Strain 3.50 %
 ISO 178
Flexural Modulus 2.90 GPa
421 ksi
ISO 178
Shear Modulus 0.275 GPa

@Temperature 120 °C
 39.9 ksi

@Temperature 248 °F
 Dynamic; ISO 11403-1 -2
0.5547 GPa

@Temperature 70.0 °C
 80.45 ksi

@Temperature 158 °F
 Dynamic; ISO 11403-1 -2
0.9459 GPa

@Temperature 20.0 °C
 137.2 ksi

@Temperature 68.0 °F
 Dynamic; ISO 11403-1 -2
1.1421 GPa

@Temperature -20.0 °C
 165.65 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
1.3715 GPa

@Temperature -50.0 °C
 198.92 ksi

@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Secant Modulus 0.475 GPa

@Strain 8.1495 %,
Temperature 80.0 °C
 68.9 ksi

@Strain 8.1495 %,
Temperature 176 °F
 ISO 11403-1 -2
0.501 GPa

@Strain 6.0764 %,
Temperature 100 °C
 72.7 ksi

@Strain 6.0764 %,
Temperature 212 °F
 ISO 11403-1 -2
0.618 GPa

@Strain 9.50 %,
Temperature 40.0 °C
 89.6 ksi

@Strain 9.50 %,
Temperature 104 °F
 ISO 11403-1 -2
0.716 GPa

@Strain 10.6 %,
Temperature 0.000 °C
 104 ksi

@Strain 10.6 %,
Temperature 32.0 °F
 ISO 11403-1 -2
0.746 GPa

@Strain 8.90 %,
Temperature 23.0 °C
 108 ksi

@Strain 8.90 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.761 GPa

@Strain 3.06 %,
Temperature 100 °C
 110 ksi

@Strain 3.06 %,
Temperature 212 °F
 ISO 11403-1 -2
0.790 GPa

@Strain 10.5 %,
Temperature -20.0 °C
 115 ksi

@Strain 10.5 %,
Temperature -4.00 °F
 ISO 11403-1 -2
0.82593 GPa

@Strain 4.0748 %,
Temperature 80.0 °C
 119.79 ksi

@Strain 4.0748 %,
Temperature 176 °F
 ISO 11403-1 -2
0.999 GPa

@Strain 0.86806 %,
Temperature 100 °C
 145 ksi

@Strain 0.86806 %,
Temperature 212 °F
 ISO 11403-1 -2
1.1125 GPa

@Strain 4.80 %,
Temperature 40.0 °C
 161.36 ksi

@Strain 4.80 %,
Temperature 104 °F
 ISO 11403-1 -2
1.35 GPa

@Strain 5.30 %,
Temperature 0.000 °C
 196 ksi

@Strain 5.30 %,
Temperature 32.0 °F
 ISO 11403-1 -2
1.36 GPa

@Strain 1.0187 %,
Temperature 80.0 °C
 198 ksi

@Strain 1.0187 %,
Temperature 176 °F
 ISO 11403-1 -2
1.37 GPa

@Strain 4.40 %,
Temperature 23.0 °C
 199 ksi

@Strain 4.40 %,
Temperature 73.4 °F
 ISO 11403-1 -2
1.67 GPa

@Strain 4.50 %,
Temperature -20.0 °C
 242 ksi

@Strain 4.50 %,
Temperature -4.00 °F
 ISO 11403-1 -2
2.10 GPa

@Strain 3.81 %,
Temperature -40.0 °C
 305 ksi

@Strain 3.81 %,
Temperature -40.0 °F
 ISO 11403-1 -2
2.21 GPa

@Strain 1.20 %,
Temperature 40.0 °C
 320 ksi

@Strain 1.20 %,
Temperature 104 °F
 ISO 11403-1 -2
2.81 GPa

@Strain 1.10 %,
Temperature 23.0 °C
 407 ksi

@Strain 1.10 %,
Temperature 73.4 °F
 ISO 11403-1 -2
3.15 GPa

@Strain 1.30 %,
Temperature 0.000 °C
 457 ksi

@Strain 1.30 %,
Temperature 32.0 °F
 ISO 11403-1 -2
3.80 GPa

@Strain 0.527 %,
Temperature -20.0 °C
 550 ksi

@Strain 0.527 %,
Temperature -4.00 °F
 ISO 11403-1 -2
4.20 GPa

@Strain 0.476 %,
Temperature -40.0 °C
 609 ksi

@Strain 0.476 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1A
Charpy Impact Unnotched 30.0 J/cm²
143 ft-lb/in²
ISO 179/1eU
24.0 J/cm²

@Temperature -30.0 °C
 114 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
ISO 179/1eA