Network Polymers PC-2109
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant |
| Manufacturer | Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers PC-2109.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Natural Flame Retardant PolycarbonateInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24 hours at 73°F; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0070 cm/cm | 0.0020 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 15 g/10 min @Load 1.20 kg, Temperature 300 °C |
15 g/10 min @Load 2.65 lb, Temperature 572 °F |
Procedure A; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 61.38 MPa | 8903 psi | chs 2 in/min; ASTM D638 |
| Flexural Strength | 90.11 MPa | 13070 psi | |
| Flexural Modulus | 2.21 GPa | 320 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 7.47 J/cm | 14.0 ft-lb/in | Test Method A (0.125 in bar); ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C | 253 °F | 0.125 in bar; ASTM D648 |
| Vicat Softening Point | 150 °C | 302 °F | 0.125 inch bar, 1 Kg; ASTM D1525 |
| Flammability, UL94 | 5VA | 5VA | 0.062 in and 0.125 in ( 0.125 in 5VA) |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 7204 LC BLK
- PolyMirae Moplen RP340R Injection Molding Grade Polypropylene
- Haynes 282® Nickel Alloy Sheet, Solution Annealed and Cold Worked
- Schott S8809 Contrast Enhancement Filter
- Chase Plastics CP Pryme® N120L (Dry) Nylon 6, 20% Glass Fiber Reinforced, Lubricated
- A. Schulman CP775-01 Molding Grade, Low Density Polyethylene
- Dr. D. Mueller Flexiso® DMD FI 14010 00100 Polyester Electrical Insulation
- DuPont Performance Polymers VTR 8650 (GBL-S) Peroxide Cured Fluoroelastomer (FKM) Formulation
- Clariant Renol 6601L Nylon 66, Lubricated
Copyright © lookpolymers.com All Rights Reserved