DuPont Performance Polymers Delrin® FG400XRD NC010 Acetal (Unverified Data**)

Category	Polymer , Thermoplastic , Acetal (POM)
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Delrin® FG400XRD NC010 Acetal (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Delrin® FG400XRD NC010 is a filled, medium viscosity acetal copolymer for injection molding. It is detected in x-ray detectors. It has been developed for consideration into applications such as parts for the food industry.Information provided by DuPont Performance Polymers

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	51.0 MPa @Temperature 23.0 °C	7400 psi @Temperature 73.4 °F	ISO 527
Elongation at Yield	7.0 % @Temperature 23.0 °C	7.0 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	3.20 GPa @Temperature 23.0 °C	464 ksi @Temperature 73.4 °F	ISO 527
Charpy Impact Unnotched	8.00 J/cm² @Temperature 23.0 °C	38.1 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.400 J/cm² @Temperature 23.0 °C	1.90 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	168 °C	334 °F	10°C/min; ISO 11357-1/-3

Processing Properties	Metric	English	Comments
Melt Temperature	205 °C	401 °F	Optimum; Injection Molding
	200 - 210 °C	392 - 410 °F	Injection Molding
Mold Temperature	90.0 °C	194 °F	optimum; Injection Molding
	80.0 - 100 °C	176 - 212 °F	Injection Molding
Drying Temperature	80.0 °C	176 °F	Injection Molding
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour	Injection Molding
Moisture Content	<= 0.20 %	<= 0.20 %	Injection Molding

Descriptive Properties	Value	Comments
Appearance	Natural Color
Forms	Pellets
Generic	Acetal (POM) Copolymer
Material Status	Preliminary Data
Processing Method	Injection Molding
Product Category	Food Contact Resins
Region Available - Global	Yes
RoHS Compliance	Contact Manufacturer
Uses	Food Applications, Non-specific