DuPont Performance Polymers Delrin® 588P NC010 Acetal Homopolymer (Unverified Data**)

Category	Polymer , Thermoplastic , Acetal (POM)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Delrin® 588P NC010 Acetal Homopolymer (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Delrin® 588P NC010 is a medium viscosity acetal homopolymer resin for injection molding. It has good thermal stability, and modifications for more precise molding (reduced warpage, good dimensional stability).Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.42 g/cc	0.0513 lb/in³	ISO 1183
Water Absorption	0.30 % @Temperature 23.0 °C	0.30 % @Temperature 73.4 °F	Equilibrium 50%RH; ISO 62, Similar to
Linear Mold Shrinkage, Flow	0.019 cm/cm @Thickness 2.00 mm	0.019 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.018 cm/cm @Thickness 2.00 mm	0.018 in/in @Thickness 0.0787 in	ISO 294-4
Melt Flow	15 g/10 min @Load 2.16 kg, Temperature 190 °C	15 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	ISO 2039/2
Tensile Strength, Yield	73.0 MPa @Temperature 23.0 °C	10600 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	25 % @Temperature 23.0 °C	25 % @Temperature 73.4 °F	nominal; ISO 527
Elongation at Yield	12 % @Temperature 23.0 °C	12 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	3.20 GPa @Temperature 23.0 °C	464 ksi @Temperature 73.4 °F	ISO 527
Charpy Impact, Notched	0.800 J/cm² @Temperature 23.0 °C	3.81 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	178 °C	352 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	97.0 °C	207 °F	ISO 75-1/-2
UL RTI, Electrical	50.0 °C @Thickness 0.800 mm	122 °F @Thickness 0.0315 in	UL 746B
	110 °C @Thickness 1.50 mm	230 °F @Thickness 0.0591 in	UL 746B
	110 °C @Thickness 3.00 mm	230 °F @Thickness 0.118 in	UL 746B
UL RTI, Mechanical with Impact	50.0 °C @Thickness 0.800 mm	122 °F @Thickness 0.0315 in	UL 746B
	85.0 °C @Thickness 1.50 mm	185 °F @Thickness 0.0591 in	UL 746B
	90.0 °C @Thickness 3.00 mm	194 °F @Thickness 0.118 in	UL 746B
UL RTI, Mechanical without Impact	50.0 °C @Thickness 0.800 mm	122 °F @Thickness 0.0315 in	UL 746B
	90.0 °C @Thickness 1.50 mm	194 °F @Thickness 0.0591 in	UL 746B
	95.0 °C @Thickness 3.00 mm	203 °F @Thickness 0.118 in	UL 746B
Flammability, UL94	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in	IEC 60695-11-10
	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	IEC 60695-11-10
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in	IEC 60695-11-10
	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	UL94
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in	UL94
	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in	UL94

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	600 V @Thickness 3.00 mm, Temperature 23.0 °C	600 V @Thickness 0.118 in, Temperature 73.4 °F	UL 746A

Processing Properties	Metric	English	Comments
Melt Temperature	215 °C	419 °F	Optimum; Injection Molding
	210 - 220 °C	410 - 428 °F	Injection Molding
Mold Temperature	90.0 °C	194 °F	optimum; Injection Molding
	80.0 - 100 °C	176 - 212 °F	Injection Molding
Drying Temperature	80.0 °C	176 °F	Injection Molding
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour	Injection Molding
Moisture Content	<= 0.20 %	<= 0.20 %	Injection Molding

Descriptive Properties	Value	Comments
Appearance	Natural Color
Extrudable - Cast Film	Yes
Extrudable - Sheet	Yes
Extrudable - Tubing	Yes
Extrudable - Wire and Cable	Yes
Features	Creep Resistance, Good
	Dimensional Stability, Good
	Fatigue Resistant
	Homopolymer
	Stiffness, High
	Strength, High
	Viscosity, Medium
Forms	Pellets
Generic	Acetal (POM) Homopolymer
Material Status	Current
Part Marking Code	>POM<	ISO 11469
Polymer Family	POM
Polymer Type	POM Homopolymer
Processing Method	Injection Molding
Product Category	Unreinforced Resins
Resin Identification	POM	ISO 1043
RoHS Compliance	Contact Manufacturer
Ultrasonic Weldable	Yes
Uses	Fasteners
	Gears
	General Purpose
	Parts, Engineering