Samsung Cheil Industries Starex® AS-0151 ABS, Unreinforced

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Samsung, Cheil Industries
Trade Name Starex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Starex® AS-0151 ABS, Unreinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Anti-staticInformation provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.08 g/cc
1.08 g/cc
ASTM D792
Melt Flow 23 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 23 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110
110
ASTM D785
Tensile Strength at Break 34.3 MPa
4970 psi
5 mm/min; ASTM D638
Tensile Strength, Yield 41.2 MPa
5970 psi
5 mm/min; ASTM D638
Elongation at Break 33 %
33 %
5 mm/min; ASTM D638
Tensile Modulus 2.26 GPa
327 ksi
5 mm/min; ASTM D638
Flexural Strength 64.7 MPa
9380 psi
2.8 mm/min; ASTM D790
Flexural Modulus 2.26 GPa
327 ksi
2.8 mm/min; ASTM D790
Izod Impact, Notched 1.96 J/cm

@Thickness 6.35 mm
 3.67 ft-lb/in

@Thickness 0.250 in
 ASTM D256
1.96 J/cm

@Thickness 3.17 mm
 3.67 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 94.0 °C

@Thickness 6.40 mm
 201 °F

@Thickness 0.252 in
 ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C

@Thickness 6.40 mm
 185 °F

@Thickness 0.252 in
 ASTM D648
Vicat Softening Point 97.0 °C
207 °F
B/50; ISO R306
100 °C
212 °F
B/120; ISO R306
Flammability, UL94 HB

@Thickness 1.00 - 3.00 mm
 HB

@Thickness 0.0394 - 0.118 in