- HOME
- POLYMER SEARCH
- Thermoset
- Rubber or Thermoset Elastomer (TSE)
- Dow Nordel® IP 4770P Highly Extended Low-Cost Hose
Dow Nordel® IP 4770P Highly Extended Low-Cost Hose
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Dow Chemical |
| Trade Name | Nordel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow Nordel® IP 4770P Highly Extended Low-Cost Hose.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FormulationNordel® IP 4770P
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.339 g/cc | 0.04837 lb/in³ | |
| Mooney Viscosity | 21 @Temperature 100 °C |
21 @Temperature 212 °F |
ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 61 | 61 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 7.00 MPa | 1020 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 492 % | 492 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00200 GPa | 0.290 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 200% Modulus | 0.00390 GPa | 0.566 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.00520 GPa | 0.754 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 31.0 kN/m | 177 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 75 % @Temperature 125 °C |
75 % @Temperature 257 °F |
Pellets cured MDR TC95 + 15 min, 70 hr; Method B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -15.0 °C | 5.00 °F | Temperature Retraction, TR-10 |
Users viewing this material also viewed the following:
- MV Labs NI250 {Ni(NH3)6}Br2 Hexaminenickel(II) bromide
- PolyOne OnFlex™ S HF 60A-3S1982 Thermoplastic Elastomer (TPE)
- Polykemi AB POLYelast TPE EC12 D55 Thermoplastic Elastomer
- PolyOne Therma-Tech™ LC-5000C TC LCP (discontinued **)
- Fujipoly Industries Sarcon® GR-HFd Gap Filler Pad
- Zircar Zirconia CeK-15 Ceria Knit Textile Insulation
- Trelleborg Emerson & Cuming Stycast® 3180M Two-Component Easy Mix Ratio Encapsulant
- CMW® 2000 AMS-T-21014 ASTM B777 High Density Machinable Tungsten
- ChevronTexaco Vistac® ISO 220 Way Oil D
- Polykemi AB POLYfill PPH T5038 Polypropylene Homopolymer, Mineral Reinforced
Copyright © lookpolymers.com All Rights Reserved