Dow PELLETHANE® 2103-75D Film Grade Thermoplastic Polyurethane Elastomer (discontinued **)

Category	Polymer , Film , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Dow PELLETHANE® 2103-75D Film Grade Thermoplastic Polyurethane Elastomer (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: PELLETHANE® 2103-75D UV stabilized, polyether based thermoplastic polyurethane elastomer has excellent hydrolytic stability and excellent resistance to micro-organisms. Applications include: Film, Tubing and belting, Geophysical wire and cable jacketing, Cell phones and PDA overmoldingData provided by Dow Chemical.Lubrizol acquired the Pellethane product line from Dow in 2009.

Physical Properties	Metric	English	Comments
Specific Gravity	1.21 g/cc	1.21 g/cc	ASTM D792
Linear Mold Shrinkage	0.0030 - 0.0080 cm/cm @Thickness 1.59 mm	0.0030 - 0.0080 in/in @Thickness 0.0625 in	plaque
Linear Mold Shrinkage, Transverse	0.0030 - 0.0070 cm/cm @Thickness 1.59 mm	0.0030 - 0.0070 in/in @Thickness 0.0625 in	plaque
Melt Index of Compound	28 g/10 min @Load 5.00 kg, Temperature 224 °C	28 g/10 min @Load 11.0 lb, Temperature 435 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	72 - 80	72 - 80	ASTM D2240
Tensile Strength, Ultimate	40.0 MPa	5800 psi	ASTM D412
Elongation at Break	380 %	380 %	ASTM D412
50% Modulus	0.0305 GPa	4.42 ksi	ASTM D412
100% Modulus	0.0313 GPa	4.54 ksi	ASTM D412
Flexural Modulus	1.31 GPa	190 ksi	ASTM D790
Tear Strength	257 kN/m	1470 pli	Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles	55	55	H-22 wheel (coarser); ASTM D1044
Tensile Set	40 %	40 %	Elongation Set After Break; ASTM D412

Thermal Properties	Metric	English	Comments
CTE, linear	88.7 µm/m-°C @Temperature 20.0 °C	49.3 µin/in-°F @Temperature 68.0 °F	ASTM D696
Vicat Softening Point	116 °C	241 °F	ASTM D1525

Processing Properties	Metric	English	Comments
Processing Temperature	204 - 221 °C	399 - 430 °F	Optimum Extrusion Temperature
Melt Temperature	210 - 227 °C	410 - 441 °F