Huntsman IROGRAN® A 85 P 5350 TPU-Polyester
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 85 P 5350 TPU-Polyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN A 85 P 5350 is a flame-retardant, halogen-free, polyether based thermoplastic polyurethane intended for extrusion and injection molding applications. IROGRAN A 85 P 5350 is part of the HUNTSMAN technical extrusion product range and offers a specially designed, flexible material with a broad processing window particularly suitable for the preparation of cable jacketing where enhanced fire retardancy is required. Performance Features: High tensile strength Excellent wear performance Excellent hydrolysis & microbial resistance Good low temperature flexibility Halogen free UL 94 Classification V2 (internal testing)Information provided by Alliance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | Injection molded parts |
| Melt Index of Compound | 36 g/10 min @Load 21.6 kg, Temperature 190 °C |
36 g/10 min @Load 47.6 lb, Temperature 374 °F |
MVR, [cm<sup>3</sup>/10 min] |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 89 | 89 | Injection molded parts; ASTM D2240 |
| Hardness, Shore D | 37 | 37 | Injection molded parts; ASTM D2240 |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | Injection molded parts; DIN 53504 |
| Elongation at Break | 690 % | 690 % | Injection molded parts; DIN 53504 |
| 100% Modulus | 0.00780 GPa | 1.13 ksi | Injection molded parts; DIN 53504 |
| 300% Modulus | 0.0113 GPa | 1.64 ksi | Injection molded parts; DIN 53504 |
| Tear Strength | 99.9 kN/m | 570 pli | Injection molded parts; ASTM D624 |
| Abrasion | 40 | 40 | mm<sup>3</sup>, Injection molded; DIN 53516 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Middle Barrel Temperature | 160 - 200 °C | 320 - 392 °F | Extrusion |
| Nozzle Temperature | 170 - 205 °C | 338 - 401 °F | Extrusion |
| 200 - 210 °C | 392 - 410 °F | Injection | |
| Adapter Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Die Temperature | 175 - 205 °C | 347 - 401 °F | Extrusion |
| Melt Temperature | 190 - 205 °C | 374 - 401 °F | Injection |
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heating Zone | 170-210°C | Injection |
Users viewing this material also viewed the following:
- Sharadaa Ceramics HFI Insulation Brick
- SABIC Innovative Plastics NORYL GTX GTX954 PPE+PA (Europe-Africa-Middle East)
- A. Schulman PP 1248-01 Polypropylene High-Flow Homopolymer Polypropylene
- DuPont Performance Polymers Zytel® HTN 54G35HSLR BK031 Polyphthalamide (PPA) (Unverified Data**)
- 3M Cold Seal® 4130 Polyethylene Tape
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 40 PHR N550 (FEF) Filler
- Abatron 8602-2 A/B Carbon-Filled Electrically Conductive Epoxy Compound
- Borealis HF136MO Polypropylene
- Master Bond EP30M4LV Chemically Resistant, Low Viscosity Adhesive
Copyright © lookpolymers.com All Rights Reserved