- Diamond Polymers ASA/PC FA-30
Diamond Polymers ASA/PC FA-30
| Category | Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ASA/PC FA-30.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: ASA Weatherable Polymer, Injection Molding Grade, Flame RetardantInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 0.70 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.70 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 2.6 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.6 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 103 | 103 | ASTM D785 |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.25 GPa | 327 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm | 10.0 ft-lb/in | Test Method A (0.125 in bar); ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 107 °C | 225 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| Vicat Softening Point | 120 °C | 248 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 238 - 257 °C | 460 - 495 °F | |
| Middle Barrel Temperature | 238 - 257 °C | 460 - 495 °F | |
| Front Barrel Temperature | 238 - 254 °C | 460 - 490 °F | |
| Nozzle Temperature | 238 - 254 °C | 460 - 490 °F | |
| Melt Temperature | 227 - 249 °C | 440 - 480 °F | Melt temperatures above 490°F are not recommended, and may result in color shifts and or thermal instability. |
| Mold Temperature | 60.0 - 82.2 °C | 140 - 180 °F | Higher mold temperature can aid flow in processing, provides a better surface finish, and creates less residual stress in the finished products. |
| Drying Temperature | 90.6 - 98.9 °C | 195 - 210 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | <= 0.10 % | <= 0.10 % | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi |
Users viewing this material also viewed the following:
- Nye Lubricants 774VLF (NG) Synthetic Oil
- Kotec Carbotex K-40UV Polycarbonate, General Purpose, UV Stability Grade
- Loctite® 680 High Strength/High Viscosity Retaining Compound
- Cossa Polimeri ESTAPROP H 0540 GFC Polypropylene, 20% Glass Filled
- ExxonMobil LLDPE L L6101RQ Linear Low Density Polyethylene Resin (European Grade)
- Dow DOWLEX™ 2500 Linear Low Density Polyethylene, Narrow MW Distribution
- 3M OFM2402 Outdoor UL Recognized Silver Polyester Label Product
- DuPont™ Surlyn® 9730 Ionomer Resin, Zinc (discontinued **)
- Overview of materials for Polypropylene, Film Grade
Copyright © lookpolymers.com All Rights Reserved