Abatron AboCast 8-8/Abocure 8-8 Epoxy (discontinued **)

Category	Polymer , Thermoset , Epoxy
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Abatron AboCast 8-8/Abocure 8-8 Epoxy (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

2-part solvent-free dielectric epoxy casting compound.Processing: 100/50 ratio (pbw); Gel time, 1 lb. (2.2 kg): 135 minutes; cures in 16 hours at 25°C (77°F); postcure: 2 hours at 100°C (212°F).Applications: solventless casting, adhesive, and coating.

Physical Properties	Metric	English	Comments
Water Absorption	0.27 %	0.27 %	in 24 hours.
Viscosity Measurement	470	470

Mechanical Properties	Metric	English
Hardness, Shore D	80	80
Tensile Strength, Ultimate	39.3 MPa	5700 psi
Elongation at Break	8.0 %	8.0 %
Flexural Strength	59.98 MPa	8699 psi
Izod Impact, Notched	0.363 J/cm	0.680 ft-lb/in

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	50.0 °C	122 °F	Deflection temperature; load unknown.

Electrical Properties	Metric	English
Electrical Resistivity	<= 1.00e+9 ohm-cm @Temperature 93.3 °C	<= 1.00e+9 ohm-cm @Temperature 200 °F
	5.20e+10 ohm-cm @Temperature 65.6 °C	5.20e+10 ohm-cm @Temperature 150 °F
	8.80e+14 ohm-cm @Temperature 25.0 °C	8.80e+14 ohm-cm @Temperature 77.0 °F
Dielectric Constant	3.54 @Frequency 1e+6 Hz	3.54 @Frequency 1e+6 Hz
Dissipation Factor	0.012 @Frequency 1e+6 Hz	0.012 @Frequency 1e+6 Hz

Processing Properties	Metric	English	Comments
Processing Temperature	25.0 °C	77.0 °F	Curing time: 16 hours; Postcure: 2 hours/100°C (212°F)